Extraction of Lanthanum and Cerıum from a Bastnasite Ore By Direct Acidic Leaching
(Chamber of Mining Engineers of Turkey, 2020) Kursunoglu, Sait; Top, S.; Hussaini, Shokrullah; Gokcen, H. S.; Altiner, Mahmut; Ozsarac, Safak; Kaya, Muammer
The extraction of lanthanum (La) and cerium (Ce) from a bastnasite ore by direct acidic leaching was investigated. The effects of acid concentration and leaching temperature on the extraction of La and Ce from the ore were tested. Using nitric (NHO3), more than 85% of the La and Ce were simultaneously extracted into leach solution whereas the La and Ce dissolutions were determined as less than 85% by using sulfuric acid (H2SO4). The La dissolution exceeded 90% by using hydrochloric acid (HCl); however, the Ce dissolution remained below 85% under the following conditions: solid-to-liquid ratio of 20% (w/v), the acid concentration of 20%, leaching temperature of 25°C and leaching time of 1 h. The result revealed that HNO3 could be used as a solvent for the maximum simultaneous extraction of the La and Ce from the bastnasite ore. The leaching temperature had no crucial effect on the dissolution of La and Ce when HNO3 or HCl solutions were preferred as a solvating agent. However, the leaching temperature had a slight positive effect on the dissolutions of La and Ce when H2SO4 was used as a solvent. © 2023 Elsevier B.V., All rights reserved.
Citation - Scopus: 2
Kalsitik ve Dolomitik Kireçtaşlarının Çimentolu Macun Dolgunun Çevresel Davranışına Etkisi
(Chamber of Mining Engineers of Turkey, 2022) Yılmaz, Tekin; Ercikdi, Bayram
To enhance the strength and stability of cemented paste backfill (CPB), many alkaline materials are utilised as replacement or additive to binder or tailings in CPB. However, the effect of these materials on groundwater pollution of CPB needs to be comprehensively investigated. In this study, effects of the utilization of calcitic and dolomitic limestone (CL and DL) as replacement (10 wt.%) to sulphide mine tailings (S-MT) in CPB mixture on the long-term environmental behaviour of CPB were investigated. For this purpose, CPB samples (CPBs) were subjected to dynamic tank leaching tests over 360-days and the analyses of pH, sulphate (SO4 2-) and heavy metals (HMs) on the leachates were carried out. The effects of mineralogy and microstructure on the environmental behavior of CPBs were also examined by X-ray diffractometry and porosity tests. The findings showed that with the utilization of CL and DL, the pH of leachates remained at alkaline levels and the release of SO4 2- was significantly reduced. Furthermore, the denser microstructure in CPBs of CL and DL contributed to be prevented or be remarkably reduced the HMs-releases (except Cu, Mo and Pb). The results reveal that the mechanical properties of CPB as well as its impact on the groundwater pollution should be carefully evaluated. © 2022 Elsevier B.V., All rights reserved.
Manganzı Demir Cevherinden Manganın Çözündürülmesinde Farklı İndirgeme Maddelerinin Etkisi
(Chamber of Mining Engineers of Turkey, 2022) Top, S.; Altiner, Mahmut; Kursunoglu, Sait
IIn this paper, the manganese extraction from a manganiferous iron ore was investigated using reductive leaching. Various chemicals were used as a reducing agent to leach manganese selectively from the ore in the presence of sulfuric acid (H2SO4) solution. Firstly, optimum dissolution values were determined for selective manganese dissolution without using a reducing agent. As it was aimed at the selective extraction of manganese from the ore, the reductive leaching tests were conducted by adding the reducing agents under the following optimal parameters: a leaching time of 1 h, a stirring speed of 300 rpm, a temperature of 70°C, a sulfuric acid concentration of 1 M where the ore was leached with an extraction ratio of 11.54% Mn and 2.16% Fe. Manganese was dissolved with high efficiencies (up to 97.46%) from the ore by using different organic compounds (tartaric acid (C4H6O6), oxalic acid (C2H2O4), citric acid (C6H8O7), glucose (C6H12O6), sucrose (C12H22O11), and maleic acid (C4H4O4)) as the reducing agents. © 2022 Elsevier B.V., All rights reserved.
Citation - Scopus: 2
Zeolite Synthesis by Alkali Fusion Method Using Two Different Fly Ashes Derived From Turkish Thermal Power Plants
(Chamber of Mining Engineers of Turkey, 2020) Top, S.; Vapur, Hüseyin
In this study, Faujasite (Na-LSX) (3.5(Ca0.3)3.5(Na0.6)3.5(Mg0.1)Al7Si17O48 32(H2O)) type zeolites and Ca-Filipsite (CaK0.6Na0.4Si5.2Al2.8O16 6(H2O)) type zeolites were produced from Sugözü Thermal Power Plant and Çatalaǧzi Thermal Power Plant fly ashes by alkali fusion method followed by water leaching, respectively. In these methods, fly ashes and sodium hydroxide (NaOH) were mixed in certain proportions and sintered at 600°C in ash furnace. Then, zeolites were obtained from the ground materials after water leaching and solid/liquid separation, respectively. Cation Exchange Capacity (CEC), X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Fourier-Transform Infrared Spectroscopy (FTIR), X-Ray Fluorescence (XRF) and Atomic Absorption Spectrometer (AAS) analyses were used to characterize the synthesized zeolites. The zeolites synthesized with Sugözü fly ashes in a ratio of 1:2 had 136.93 meq/100 g CEC, whereas the CEC of synthesized zeolite from Çatalaǧzi fly ashes was found to be 247.88 meq/100 g. As a result, zeolites, which can be used as wastewater treatment agent, energy storage material, catalyst and separator, were synthesized by using 2 different Class F fly ash. © 2023 Elsevier B.V., All rights reserved.