  • Article
    Citation - WoS: 10
    Citation - Scopus: 11
    Production of Mn3O4 Nanoparticles From a Manganiferous Iron Ore via Reductive Leaching, Precipitation, and Calcination
    (Elsevier, 2022-02) Altiner, Mahmut; Top, Soner; Bouchekrit, Chafia; Kursunoglu, Sait
    The synthesis of Mn3O4 nanoparticles from a manganiferous iron ore through reductive leaching, precipitation, and calcination was investigated. The reductive leaching results showed that Mn (99.9%) was almost completely extracted into the leaching solution along with a substantial amount of Mg (99.9%), Al (99.5%), Ca (80%), and Fe (22.9%) under the following conditions: 30 g/L tartaric acid as a reducing agent, 1 M HCl solution, leaching temperature of 90 ?, and leaching duration of 3 h. In the first precipitation step, Fe and Al were expelled from the pregnant leach solution by the addition of NaOH prior to conducting the precipitation experiments for the production of manganese carbonate (MnCO3) particles from the purified solution. In the second precipitation step, MnCO3 particles were produced using sodium carbonate (Na2CO3) as the precipitating agent. The effects of parameters such as reaction temperature, Na2CO3 concentration, and experimental duration were investigated using the Taguchi approach. Manganse(II) was precipitated in the form of MnCO3 particles (97.4%) under the following conditions: a temperature of 30 ?C, Na2CO3 concentration of 0.014 mol/L, and duration of 30 min. The precipitate was observed to have a structure similar to that of rhodochrosite (MnCO3). Thermogravimetric/ differential thermal analyses were subsequently performed in three different atmospheres (air, oxygen, and nitrogen) to select a suitable atmosphere for calcination. The experimental results indicated the formation of hausmannite (Mn3O4) with a purity of 97.5% Mn3O4, 0.42% MgO, 1.66% CaO, and 0.34% FeO. The specific surface area, particle size, Curie temperature, magnetisation, coercivity, and remanence ratio of the final product obtained via 3 h of calcination at 350 C were estimated to be 133.3 m(2)/g, < 142.2 nm, 56 K, 10.10 Am-2/kg, 0.35 T, and 0.19, respectively. The characterisation results revealed the excellent low-temperature ferromagnetic properties of the produced Mn3O4 nanoparticles.
  • Article
    Citation - WoS: 14
    Citation - Scopus: 18
    Pb-Zn Recovery From a Malic Leach Solution of a Carbonate Type Ore Flotation Tailing by Precipitation and Solvent Extraction
    (Elsevier, 2021-10) Hussaini, Shokrullah; Tita, Angela Manka; Kursunoglu, Sait; Top, Soner; Ichlas, Zela Tanlega; Kar, Umut; Kaya, Muammer
    The recovery of zinc and lead from a malic leach solution of a carbonate type ore flotation tailing by precipitation with sulfuric acid followed by solvent extraction using di(2-ethylhexyl)phosphoric acid (D2EHPA) as extractant was investigated. The separation of lead via precipitation was essentially complete from the malic acid leach solution by adding sulphuric acid to reach a pH of 0.25 at 25 degrees C. The precipitate product was identified by XRD as anglesite (PbSO4). The pregnant leach solution after lead precipitation was then subjected to solvent extraction using D2EHPA. The optimum solvent extraction conditions were determined as 10% D2EHPA concentration, 25 degrees C temperature, 10 min contact time and phase ratio of unity. Under these conditions, 99.3% of zinc was extracted into the organic phase at a pH of 4.2 in a single contact alongside a substantial amount of Ca (76.6%), and minor amounts of Fe (19.2%) and Mg (18%). Complete stripping of zinc and calcium from the loaded organic solution along with 47.8% of Mg was achieved at a pH 0.5 under room temperature. No iron stripping was observed from the loaded organic. The zinc content in the loaded strip solution could be enriched and then sent to the electrowinning (EW) stage. It is noted that the calcium and magnesium impurities in the loaded strip solution had no adverse effect on the zinc EW process. Based on the experimental results, a flowsheet was proposed for the recovery of Pb and Zn from the malic acid leach solution. With the proposed precipitation and solvent extraction process, two different material streams are produced.