Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
2 results
Search Results
Article Citation - WoS: 2Citation - Scopus: 2Fully Inorganic Colloidal CsPbBr3 Perovskite Nanocrystals with Zn-Doping and Metal Oxide Encapsulation for Luminescent Display Panels(Amer Chemical Soc, 2025-11-07) Khorasani, Azam; Soheyli, Ehsan; Mutlugun, EvrenPerovskite nanocrystals (PeNCs) are emerging as exceptional materials due to their high photoluminescence quantum yield, tunable bandgap, and excellent charge carrier mobility, enabling a wide range of colors and promising applications in optoelectronics and photovoltaics. Despite their advantages, PeNCs face stability challenges caused by environmental factors. In the presented study, a facile and versatile colloidal hot-injection method was used to apply the beneficial aspects of Zn-doping in cesium lead bromide (CsPbBr3) PeNCs. The uniform platelet-shaped Zn-doped CsPbBr3 PeNCs were prepared by doping with a 0.1 molar ratio of zinc-oleate solution in the perovskite precursors during synthesis. Then, zinc-oxide (ZnO) and nickel-oxide (NiO) coating layers were utilized separately to effectively reduce surface defects, encapsulate PeNCs, and improve their stability issues. To fabricate the coated PeNCs with metal oxides, zinc acetate and nickel(II) acetate tetrahydrate solutions were prepared individually and added to the crude perovskite solutions. The quantum yield of Zn-doped CsPbBr3 (CsPb1-xZnxBr3) PeNCs coated with ZnO increased from 50% for bare CsPbBr3 to over 84%, while NiO-coated PeNCs exhibited a higher yield of 90% both of which remarkably enhanced the emission stability. Moreover, NiO coatings represented a proper protection against surface imperfections and improved resistance to external stimuli. The combination of facile/effective preparation method, excellent emission efficiency, and reliable emission stability nominates the prepared colloidal composite for display pixels, detectors, and lasers.Article Citation - WoS: 5Citation - Scopus: 5Enhanced Photoluminescence Emission Intensity and Stability of Deep Blue-Emissive (Et 3 Nh)pbbr 3 Perovskite Nanocrystals by Using Metal-Organic Frameworks(Elsevier Sci Ltd, 2024-08) Hemmati, Tayebeh; Naghipour, Ali; Sahraei, Reza; Soheyli, EhsanThe primary obstacle faced by researchers in the field of luminescent metal-halide perovskites is their inherent instability, prompting a shift in focus towards enhancing the stability of perovskite nanocrystals (PNCs). One of the promising approaches to address this challenge involves the utilization of metal-organic frameworks (MOFs) to fabricate PNCs@MOF composites. The present study reports a facile and low-cost colloidal strategy to prepare (Et3NH)PbBr3 PNCs followed by their encapsulation within UiO-67 to enhance their photoluminescence (PL) emission stability. The PNCs and modified UiO-67 were prepared separately via simple and efficient ligandassisted reprecipitation (LARP) and hydrothermal methods, respectively. After modification of the UiO-67, the pore sizes experienced a substantial increase from 1.90 to 28.84 nm which significantly facilitated the localization of PNCs within the porous matrix. Under a full survey of experimental conditions, the resulting (Et3NH) PbBr3@UiO-67 composite exhibited a bright deep-blue emission at around 410 nm with an emission quantum yield of 52 %. The emission durability of the fabricated PNCs@MOF composites was assessed against temperature and long-time of storage, confirming the superior advantages of MOF even at elevated temperatures of up to 100 degrees C. The stable and luminous deep-blue emission displayed by the PNCs@MOF composites in this investigation, offers a promising advancement in materials development for optoelectronic applications.