Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
50 results
Search Results
Article Citation - WoS: 2Citation - Scopus: 1Fully Inorganic Colloidal CsPbBr3 Perovskite Nanocrystals with Zn-Doping and Metal Oxide Encapsulation for Luminescent Display Panels(Amer Chemical Soc, 2025-11-07) Khorasani, Azam; Soheyli, Ehsan; Mutlugun, EvrenPerovskite nanocrystals (PeNCs) are emerging as exceptional materials due to their high photoluminescence quantum yield, tunable bandgap, and excellent charge carrier mobility, enabling a wide range of colors and promising applications in optoelectronics and photovoltaics. Despite their advantages, PeNCs face stability challenges caused by environmental factors. In the presented study, a facile and versatile colloidal hot-injection method was used to apply the beneficial aspects of Zn-doping in cesium lead bromide (CsPbBr3) PeNCs. The uniform platelet-shaped Zn-doped CsPbBr3 PeNCs were prepared by doping with a 0.1 molar ratio of zinc-oleate solution in the perovskite precursors during synthesis. Then, zinc-oxide (ZnO) and nickel-oxide (NiO) coating layers were utilized separately to effectively reduce surface defects, encapsulate PeNCs, and improve their stability issues. To fabricate the coated PeNCs with metal oxides, zinc acetate and nickel(II) acetate tetrahydrate solutions were prepared individually and added to the crude perovskite solutions. The quantum yield of Zn-doped CsPbBr3 (CsPb1-xZnxBr3) PeNCs coated with ZnO increased from 50% for bare CsPbBr3 to over 84%, while NiO-coated PeNCs exhibited a higher yield of 90% both of which remarkably enhanced the emission stability. Moreover, NiO coatings represented a proper protection against surface imperfections and improved resistance to external stimuli. The combination of facile/effective preparation method, excellent emission efficiency, and reliable emission stability nominates the prepared colloidal composite for display pixels, detectors, and lasers.Article Citation - WoS: 13Citation - Scopus: 11Understanding the Effect of Symmetry Breaking on Plasmon Coupling From TDDFT(Amer Chemical Soc, 2021-05-26) Alkan, Fahri; Aikens, Christine M.We perform a time-dependent density functional theory (TDDFT) investigation for the optical properties of nanorod assemblies for different sizes (Ag-10, Ag-59, and Ag-139), interparticle distances, and orientations with a focus on the effect of symmetry breaking via an angle on plasmon coupling. For the model systems, the angle (theta) between the particles is varied between 0 and 180 degrees, where theta = 0 degrees and theta = 180 degrees correspond to symmetric side-by-side and end-to-end orientations of the nanorods, respectively. Our analysis reveals that for a sufficiently large interparticle distance (r > 0.7 nm), where the wave-function overlap between monomers is negligible, TDDFT results agree quite well with the predictions of the dipole-dipole interaction model for the intensity of the different modes of coupled plasmons. For smaller gap distances (0.4-0.5 nm), a charge-transfer plasmon (CTP) mode occurs for the symmetry broken case of the Ag-10 dimer. For the assemblies of larger nanorods, however, the CTP mode is predicted to be less pronounced, especially for the cases where the deviation from the end-to-end geometry is larger than 30 degrees. The orbital overlap and configuration-interaction analyses show that these results are related to the fact that the relative overlap strength between monomeric energy levels is significantly reduced for symmetry-broken orientations of larger nanorods.Article Citation - WoS: 19Citation - Scopus: 19Understanding and Tailoring Excited State Properties in Solution-Processable Oligo(p-Phenyleneethynylene)s: Highly Fluorescent Hybridized Local and Charge Transfer Character via Experiment and Theory(Amer Chemical Soc, 2021-10-13) Usta, Hakan; Cosut, Bunyemin; Alkan, FahriRod-shaped oligo(p-phenyleneethynylene) (OPE) offers an attractive p-framework for the development of solution-processable highly fluorescent molecules having tunable hybridized local and charge transfer (HLCT) excited states and (reverse) intersystem crossing ((R)ISC) channels. Herein, an HLCT oligo(p-phenyleneethynylene) library was studied for the first time in the literature in detail systematically via experiment and theory. The design, synthesis, and full characterization of a new highly fluorescent (Phi(PL-solution) similar to 1) sky blue emissive 4',4 ''-((2,5-bis((2-ethylhexyl)oxy)-1,4-phenylene)bis(ethyne-2,1-diyl))bis(N,N-diphenyl-[1,1'-bi-phenyl]-4-amine) (2EHO-TPA-PE) was also reported. The new molecule consists of a D'-Ar-pi-D-pi-Ar-D' molecular architecture with an extended pi-spacer and no acceptor unit, and detailed structural, physicochemical, single-crystal, and optoelectronic characterizations were performed. A high solid-state quantum efficiency (Phi(PL-solution) similar to 0.8) was achieved as a result of suppressed exciton-phonon/vibronic couplings (no pi-pi interactions and multiple (14 per dimeric form) strong C-H center dot center dot center dot pi interactions). Strong solution-phase/solid-state dipole-dependent tunable excited state behavior (local excited (LE) -> HLCT -> charge transfer (CT)) and decay dynamics covering a wide spectral region were demonstrated, and the CT state was observed to be highly fluorescent despite extremely large Stokes shift (similar to 130 nm)/fwhm (similar to 125 nm) and significant charge separation (0.75 charge.nm). Employing the Lippert-Mataga model, along with detailed photophysical studies and TDDFT calculations, key relationships between molecular design-electronic structure-exciton characteristics were elucidated with regards to HLCT and hot exciton channel formations. The interstate coupling between CT and LE states and the interplay of this coupling with respect to medium polarity were explored. A key relationship between excited-state symmetry breaking process and the formation of HLCT state was discussed for TPA-ended rod-shaped OPE p-systems. (R)ISC-related delayed fluorescence (tau similar to 2-6 ns) processes were evident following the prompt decays (similar to 0.4-0.9 ns) both in the solution and in the solid-state. As a unique observation, the delayed fluorescence could be tuned and facilitated via small dielectric changes in the medium. Our results and the molecular engineering perspectives presented in this study may provide unique insights into the structural and electronic factors governing tunable excited state and hot-exciton channel formations in OPEs for (un)conventional solution-processed luminescence applications.Article Citation - WoS: 18Citation - Scopus: 18Ultrahigh Vacuum Self-Assembly of Rotationally Commensurate C8-BTBT/MoS2 Mixed-Dimensional Heterostructures(Amer Chemical Soc, 2019-02-12) Liu, Xiaolong; Balla, Itamar; Sangwan, Vinod K.; Usta, Hakan; Facchetti, Antonio; Marks, Tobin J.; Hersam, Mark C.Mixed-dimensional van der Waals heterostructures combine the advantages of nanomaterials with qualitatively distinct properties such as the extended bandstructures and high charge carrier mobilities of inorganic two-dimensional materials and the discrete orbital energy levels and strong optical absorption of zero-dimensional organic molecules. The synergistic interplay between nanomaterials of distinct dimensionality has enabled a variety of unique applications such as antiambipolar transistors, sensitized photodetectors, and gate-tunable photovoltaics. Because the performance of mixed-dimensional heterostructure devices depends sensitively on the buried interfacial structure, it is of great interest to identify materials and chemistries that naturally form highly ordered heterointerfaces. Toward this end, here we demonstrate ultrahigh vacuum self-assembly of 2,7-dioctyl[1]benzothieno [3,2-b][1]benzothiophene (C8-BTBT) monolayers onto epitaxial MoS2/graphene heterostructures. With molecular-resolution scanning tunneling microscopy and spectroscopy, the resulting C8-BTBT/MoS2/graphene mixed-dimensional heterostructures are found to be rotationally commensurate with well-defined physical and electronic structures. It is further shown that the self-assembled C8-BTBT monolayers are insensitive to the structural defects and electronic perturbations of the underlying MoS2 substrate, which provides significant processing latitude. For these reasons, this work will facilitate ongoing efforts to utilize organic/MoS2/graphene mixed-dimensional heterostructures for electronic, optoelectronic, and photovoltaic applications.Article Citation - WoS: 13Citation - Scopus: 13Tuning the Shades of Red Emission in InP/ZnSe Nanocrystals With Narrow Full Width for Fabrication of Light-Emitting Diodes(Amer Chemical Soc, 2023-10-13) Soheyli, Ehsan; Bicer, Aysenur; Ozel, Sultan Suleyman; Tiras, Kevser Sahin; Mutlugun, Evren; Sahin Tiras, KevserWhile Cd-based luminescent nanocrystals (NCs) are the most mature NCs for fabricating efficient red light-emitting diodes (LEDs), their toxicity related limitation is inevitable, making it necessary to find a promising alternative. From this point of view, multishell-coated, red-emissive InP-based NCs are excellent luminescent nanomaterials for use as an emissive layer in electroluminescent (EL) devices. However, due to the presence of oxidation states, they suffer from a wide emission spectrum, which limits their performance. This study uses tris-(dimethyl-amino)-phosphine (3DMA-P) as a low-cost aminophosphine precursor and a double HF treatment to suggest an upscaled, cost-effective, and one-pot hot-injection synthesis of purely red-emissive InP-based NCs. The InP core structures were coated with thick layers of ZnSe and ZnS shells to prevent charge delocalization and to create a narrow size distribution. The purified NCs showed an intense emission signal as narrow as 43 nm across the entire red wavelength range (626-670 nm) with an emission quantum efficiency of 74% at 632 nm. The purified samples also showed an emission quantum efficiency of 60% for far-red wavelengths of 670 nm with a narrow full width of 50 nm. The samples showed a relatively long average emission lifetime of 50-70 ns with a biexponential decay profile. To demonstrate the practical ability of the prepared NCs in optoelectronics, we fabricated a red-emissive InP-based LEDs. The best-performing device showed an external quantum efficiency (EQE) of 1.16%, a luminance of 1039 cd m(-2), and a current efficiency of 0.88 cd A(-1).Article Citation - WoS: 4Citation - Scopus: 4Transparent Films Made of Highly Scattering Particles(Amer Chemical Soc, 2020-01-13) Erdem, Talha; Yang, Lan; Xu, Peicheng; Altintas, Yemliha; O'Neil, Thomas; Caciagli, Alessio; Eiser, ErikaToday, colloids are widely employed in various products from creams and coatings to electronics. The ability to control their chemical, optical, or electronic features by controlling their size and shape explains why these materials are so widely preferred. Nevertheless, altering some of these properties may also lead to some undesired side effects, one of which is an increase in optical scattering upon concentration. Here, we address this strong scattering issue in films made of binary colloidal suspensions. In particular, we focus on raspberry-type polymeric particles made of a spherical polystyrene core decorated by small hemispherical domains of acrylate with an overall positive charge, which display an unusual stability against aggregation in aqueous solutions. Their solid films display a brilliant red color due to Bragg scattering but appear completely white on account of strong scattering otherwise. To suppress the scattering and induce transparency, we prepared films by hybridizing them with oppositely charged PS particles with a size similar to that of the bumps on the raspberries. We report that the smaller PS particles prevent raspberry particle aggregation in solid films and suppress scattering by decreasing the spatial variation of the refractive index inside the film. We believe that the results presented here provide a simple strategy to suppress strong scattering of larger particles to be used in optical coatings.Article Citation - WoS: 28Citation - Scopus: 29Three-Dimensional Au-Coated Electrosprayed Nanostructured BODIPY Films on Aluminum Foil as Surface-Enhanced Raman Scattering Platforms and Their Catalytic Applications(Amer Chemical Soc, 2017-05-16) Yilmaz, Mehmet; Erkartal, Mustafa; Ozdemir, Mehmet; Sen, Unal; Usta, Hakan; Demirel, GokhanThe design and development of three-dimensional (3D) nanostructures with high surface-enhanced Raman scattering (SERS) performances have attracted considerable attention in the fields of chemistry, biology, and materials science. Nevertheless, electrospraying of organic smalt molecules on low-cost flexible substrates has never been studied to realize large-scale SERS-active platforms. Here, we report the facile, efficient, and low-cost fabrication of-Stable and reproducible Au-coated electrosprayed organic semiconductor films (Au@BDY-4TEBDY) on flexible regular aluminum foil at a large scale (5 cm X 5 cm) for practical SERS and catalytic applications. To this end, a well-designed-acceptor-donor-atceptor-type solution-processable molecular semiconductor, BDY-4T-BDY, developed by our group, is used because of its advantageous structural and electrical properties. The morphology of the electrosprayed organic film changes by solution concentration, and two different 3D morphologies with out-of-plane features are obtained. Highly uniform dendritic nanoribbons with sharp needle-like tips and vertically oriented nanoplates (similar to 50 nm thickness) are achieved when electrospraying solution concentrations of 240 and 253% w/v.(mgimL) are, respectively, used. When these electrosprayed organic films are coated with a nanoscopic thin (30 nm) Au layer, the resulting Au@BDY-4T-BDY platforms demonstrate remarkable SERS enhancement factors up to 1.7 X 10(6) with excellent Raman signal reproducibility (relative standard deviation <= 0.13) for methylene blue over the entire film. Finally, Au@BDY-4T-BDY films showed good catalytic activity for the reduction of 4-nitrophenol to 4-aminophenol with rate constants of 1.3 X 10(-2) and 9.2 X 10(-3) min(-1). Our results suggest that electrospraying of rationally designed organic semiconductor molecules on flexible substrates holds great promise to enable low-cost, solution-processed, SERS-active platforms.Article Citation - WoS: 53Citation - Scopus: 59Thickness-Tunable Self-Assembled Colloidal Nanoplatelet Films Enable Ultrathin Optical Gain Media(Amer Chemical Soc, 2020-07-31) Erdem, Onur; Foroutan, Sina; Gheshlaghi, Negar; Guzelturk, Burak; Altintas, Yemliha; Demir, Hilmi VolkanWe propose and demonstrate construction of highly uniform, multilayered superstructures of CdSe/CdZnS core/shell colloidal nanoplatelets (NPLs) using liquid interface self-assembly. These NPLs are sequentially deposited onto a solid substrate into slabs having monolayer-precise thickness across tens of cm(2) areas. Because of near-unity surface coverage and excellent uniformity, amplified spontaneous emission (ASE) is observed from an uncharacteristically thin film having 6 NPL layers, corresponding to a mere 42 nm thickness. Furthermore, systematic studies on optical gain of these NPL superstructures having thicknesses ranging from 6 to 15 layers revealed the gradual reduction in gain threshold with increasing number of layers, along with a continuous spectral shift of the ASE peak (similar to 18 nm). These observations can be explained by the change in the optical mode confinement factor with the NPL waveguide thickness and propagation wavelength. This bottom-up construction technique for thickness-tunable, three-dimensional NPL superstructures can be used for large-area device fabrication.Article Citation - WoS: 6Citation - Scopus: 7Tailored Synthesis of Iron Oxide Nanocrystals for Formation of Cuboid Mesocrystals(Amer Chemical Soc, 2021-08-02) Soran-Erdem, Zeliha; Sharma, Vijay Kumar; Hernandez-Martinez, Pedro Ludwig; Demir, Hilmi VolkanIn this work, we systematically studied the shape- and size-controlled monodisperse synthesis of iron oxide nanocrystals (IONCs) for their use as building blocks in the formation of mesocrystals. For this aim, on understanding the influence of the oleic acid concentration, iron-oleate concentration, and heating rate on the synthesis of robust and reproducible IONCs with desired sizes and shapes, we synthesized highly monodisperse similar to 11 nm sized nanocubes and nanospheres. Magnetic measurements of both cubic and spherical IONCs revealed the presence of mixed paramagnetic and superparamagnetic phases in these nanocrystals. Moreover, we observed that the magnetic moments of the nanocubes are more substantial compared to their spherical counterparts. We then demonstrated a simple magnetic-field-assisted assembly of nanocubes into three-dimensional (3D) cuboid mesocrystals while nanospheres did not form any mesocrystals. These findings indicate that small cubic nanocrystals hold great promise as potential building blocks of 3D magnetic hierarchical structures with their superior magnetic properties and mesocrystal assembly capability, which may have high relevance in various fields ranging from high-density data storage to biomedical applications.Article Citation - WoS: 13Citation - Scopus: 13Sulfobetaine-Based Homo- and Copolymers by Raft: Cross-Linked Micelles and Aqueous Solution Properties(Amer Chemical Soc, 2022-08-04) Gurdap, Seda; Bayram, Nazende Nur; Isoglu, Ismail Alper; Isoglu, Sevil Dincer; Dinçer İşoǧlu, SevilIn this study, we describe the synthesis and aqueous solution behavior of temperature-sensitive N-(3-sulfopropyl)-N-methacroyloxyethyl-N,N-dimethylammonium betaine (SBMA) homopolymers and core cross-linked micelles (CCMs) with an SBMA shell. Reversible addition- fragmentation chain transfer polymerization has been utilized to synthesize sulfobetaine homopolymers, followed by CCM formation during copoly-merization in the presence of an acid-degradable cross-linker. First, SBMA homopolymers of varying chain lengths were synthesized, and it has been demonstrated that an increase in the chain length and concentration of the homopolymer resulted in an increase in the upper critical solution temperature (UCST). Besides, micelles showed concentration-dependent dual temperature-sensitive behavior with UCST and LCST transitions. Also, homopolymers and CCMs were characterized by FTIR, H-1-NMR, GPC, and TEM. Micelle formation and temperature sensitivity were also investigated by DLS. As a result, stabilized micelles were successfully prepared with the motivation of preventing premature drug release and achieving a pH-and temperature-controlled system. Due to their dual-responsive characteristics, the CCMs show promising potential to be used as smart drug carriers for controlled delivery.