  • Article
    Citation - WoS: 130
    Citation - Scopus: 157
    Thermal Conductivity, Compressive Strength and Ultrasonic Wave Velocity of Cementitious Composite Containing Waste PET Lightweight Aggregate (WPLA)
    (Elsevier Sci Ltd, 2013-02) Akcaozoglu, Semiha; Akcaozoglu, Kubilay; Atis, Cengiz Duran
    In this study, the influence of waste PET as lightweight aggregate (WPLA) replacement with conventional aggregate, on thermal conductivity, unit weight and compressive strength properties of concrete composite was investigated. For this purpose, five different mixtures were prepared (the control mixtures and four WPLA mixtures including 30%, 40%, 50%, and 60% waste PET aggregate by volume). Thermal conductivity (TC) coefficients of the specimens were measured with guarded hot plate apparatus according to TS ISO 8302 [1]. The thermal conductivity coefficient, unit weight and compressive strength of specimens decreased as the amount of WPLA increased in concrete. The minimum thermal conductivity value was 0.3924 W/m K, observed at 60% WPLA replacement. From this result, it was concluded that waste PET aggregates replacement with conventional aggregate in the mixture showed better insulation properties (i.e. lower thermal coefficient). Due to the low unit weight and thermal conductivity values of WPLA composites, there is a potential of using WPLA composites in construction applications. (c) 2012 Elsevier Ltd. All rights reserved.
  • Article
    Citation - WoS: 6
    Citation - Scopus: 6
    The Influence of Cement Kiln Dust on Strength and Durability Properties of Cement-Based Systems
    (Springer Heidelberg, 2022-06-06) Hakkomaz, Hadiye; Yorulmaz, Hediye; Durak, Ugur; Ilkentapar, Serhan; Karahan, Okan; Atis, Cengiz Duran
    There are very few studies in the literature on the usage of CKD in cementitious systems. This article presents the laboratory study results on the influence of cement kiln dust (CKD) on the properties of mortar made with cement kiln dust and Portland cement. The article aims to prevent CKD's (known as a hazardous waste product) damage to nature by utilizing CKD in cementitious systems and contributing to sustainability by reducing cement amount in the cementitious system. For this purpose, 5%, 10%, 15%, and 20% of CKD were replaced with cement and binary cementitious systems were formed. For all mortar mixes, the water/binder ratio was kept constant at 0.5, and the sand/binder ratio was 3. Workability, dry unit weight, water absorption ratio and porosity, flexural strength, compressive strength, abrasion, carbonation, and high-temperature resistance tests were performed on the mortar specimens. Based on the results of laboratory work, it was observed that the replacement of CKD with cement reduces the workability of fresh mortar. Compressive and flexural strengths of CKD-added mixtures were found to be equivalent or insignificantly lower than that of the control sample. The addition of CKD had a negligible effect on water absorption and porosity of samples. Besides, the residual compressive strength determined after the elevated temperature test for the sample made with CKD were found to be equivalent or higher compared to the control sample. Present laboratory studies showed that utilization of CKD in cementitious mortar system is feasible in terms of testing conducted.
  • Article
    Citation - WoS: 9
    Citation - Scopus: 11
    Evaluation of Diatomite Substitute With Thermal Power Plant Waste Fly Ash in Sustainable Geopolymer Through Life Cycle Assessment
    (Springer, 2025-02-28) Ilkentapar, Serhan; Orklemez, Ezgi; Durak, Ugur; Gulcimen, Sedat; Bayram, Savas; Uzal, Nigmet; Atis, Cengiz Duran
    This research demonstrates the potential of diatomite as a fly ash replacement to improve mechanical properties and environmental sustainability and presents it as a viable alternative for sustainable construction. Additionally, a life cycle assessment (LCA) was conducted on the produced mortars to quantitatively compare their environmental impacts using a cradle-to-gate approach. In mixtures, it was used by replacing the diatomite in the ratios of 1%, 2%, 3%, 4%, and 5% by weight of the fly ash. Workability, unit weight, flexural and compressive strength, abrasion resistance, elevated temperature resistance and microstructure analysis were carried out. The results indicated that replacing 1%, 2%, and 3% diatomite increased the compressive and flexural strength of mortars due to their higher specific surface area. Two percent replacement of diatomite provided the best results. FESEM results of 3% diatomite inclusion showed more intense and compact microstructure of geopolymer. Diatomite inclusion increased the abrasion resistance of geopolymer. Since 2% diatomite replacement was found to be optimum, the LCA results showed that geopolymer mortar with 2% diatomite has 25% lower impacts in terms of global warming potential and 10% lower impacts in terms of terrestrial ecotoxicity than conventional Portland cement mortar.
  • Article
    Citation - WoS: 8
    Citation - Scopus: 10
    Compatibility and Biomineralization Oriented Optimization of Nutrient Content in Nitrate-Reducing Microbial Self-Healing Concrete
    (MDPI, 2021-08-11) Kardogan, Beyza; Sekercioglu, Kadir; Ersan, Yusuf Cagatay
    Microbially induced calcium carbonate precipitation (MICP) can be mentioned among the popular approaches to develop a self-healing concrete. The production of dissolved inorganic carbon through microbial activity is the main precursor for MICP in concrete and it is limited by the bioavailability of the nutrients. When nutrients are added to the mortar as admixtures, their bioavailability becomes more significant for crack repair because nutrients disperse in the mortar and considerable fraction stays far from a single crack. Therefore, the determination of bioavailability of nutrients and its variation with the initial nutrient content and crack age is essential to optimize a recipe for bacteria-based self-healing concrete. This study presents the optimum nutrient content defined for nitrate-reduction-based self-healing bioconcrete. In the tests, calcium nitrate (CN) and calcium formate (CF) were combined with a CF:CN w/w ratio of 2.50. Mortar properties and bioavailability of nutrients were analysed at different nutrient doses. Moreover, the bioavailability of nutrients at different crack ages changing between 3 and 56 days was monitored. Finally, resuscitation, microbial activity and the MICP performance of nitrate reducing biogranules were tested at defined nutrient bioavailabilties. The optimum nutrient content was determined as 7.00% (CF 5.00% and CN 2.00%). The leaching rates of formate ions were twice the leaching rate of the nitrate ions at similar initial concentrations, which led to a bioavailable HCOO-/NO3-N ratio of 23 g/g in cracked mortar. Under optimum nutrient conditions, the CaCO3 precipitation yield of nitrate reducing biogranules was recorded as 1.5 g CaCO3/g HCOO- which corresponded to 68% C precipitation efficiency.
  • Article
    Citation - WoS: 4
    Citation - Scopus: 4
    Characterization of Limestone Calcined Clay Cement Made With Calcium Sulfoaluminate Clinker
    (Springer int Publ Ag, 2024-07-02) Atasever, Muhammet; Erdogan, Sinan Turhan
    This study concentrated on producing limestone calcined clay calcium sulfoaluminate cement by replacing portland cement in limestone calcined clay cement with calcium sulfoaluminate cement, with the goal of increasing the early strength of limestone calcined clay cement. The mineralogy and microstructures of hydrating pastes were investigated using x-ray diffraction and scanning electron microscopy. Heat evolution was studied using isothermal calorimetry. Strength development and workability were assessed on mortar samples. The 1 day strengths of limestone calcined clay calcium sulfoaluminate cement samples exceeded those of limestone calcined clay cement by similar to 30-80%, though its strength gain slows significantly after 1 day due to the lack of calcium silicates, affecting pH and clay dissolution. Despite this, the strength development of limestone calcined clay calcium sulfoaluminate cement, when adjusted for CO2 emissions, is comparable to limestone calcined clay cement. Additionally, limestone calcined clay calcium sulfoaluminate cement provides a 10-15% higher flow and exhibits a lower heat of hydration beyond 12 h, while maintaining a production cost similar to that of limestone calcined clay cement.
  • Article
    Citation - WoS: 8
    Citation - Scopus: 9
    A New Quantitative Welding Degree Classification for Ignimbrites
    (Springer, 2023-06-28) Akin, Mutluhan; Topal, Tamer; Dincer, Ismail; Akin, Muge K.; Ozvan, Ali; Orhan, Ahmet; Orhan, Ayse
    As a pyroclastic rock type, ignimbrites may reveal varying degrees of welding depending on the temperature (> 535 celcius) and overburden pressure conditions during its formation. The welding degree of ignimbrites increases as the formation temperature and the thickness of the overburden deposit in the depositional environment escalate, which are the most crucial factors controlling the rate of welding in ignimbrites. With the increasing temperature, plastic deformation is observed in ignimbrites and the glassy minerals are being welded. Furthermore, the thickness of the overburden causes the deformation of the ash matrix in ignimbrites at the lower sections and the pumice grains are flattened at different rates. An increase in the degree of welding of ignimbrites causes an improvement in the physical and mechanical properties of the rock material as well. Within the scope of this research, petrographical, mineralogical, and geochemical studies were carried out on a total of 16 different ignimbrite types, which have different color and texture properties, obtained from three different regions of Turkey (Kayseri, Nevsehir, Ahlat) where ignimbrites extensively crop out, and the physical and mechanical properties of these samples were revealed. Consequently, a new welding classification was developed for ignimbrites considering the uniaxial compressive strength and dry unit weight. The proposed welding classification consists of six classes ranging from non-welded to highly welded. When the welding degrees of the selected ignimbrites are evaluated, Kayseri ignimbrites mostly exhibit moderate welding characteristics. Nevsehir ignimbrites, on the other hand, have a low welding degree whereas the degree of welding in Ahlat ignimbrites may vary from low to high. Additionally, long and short axis lengths of pumice grains in the ignimbrite specimens were determined by measuring under the microscope, and shape ratios were determined by different shape parameter evaluation methods. As a result, it has been concluded that the pumice grains in Kayseri and Ahlat ignimbrites have a more lenticular structure than the pumice grains in Nevsehir ignimbrites. Eventually, the welding degree classes of ignimbrites and the classification developed by using threshold values of the oblateness ratio (OR) values of pumice grains at different welding degrees are quite compatible. The proposed welding degree classification is of great importance in the selection of ignimbrites widely used as dimension stone and in terms of engineering classification of this rock type as well as it will guide to the scientific studies to be performed on ignimbrites with varying physical and mechanical properties.