Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
2 results
Search Results
Article Citation - WoS: 9Citation - Scopus: 6Separation of Fe and Mn From Manganiferous Iron Ores via Reductive Acid Leaching Followed by Magnetic Separation(Springer, 2019-08-01) Top, S.In this study, a process to separate manganese and iron from manganiferous iron ores by reductive acid leaching followed by magnetic separation was conceived and experimentally tested. In the leaching process, sulfuric acid was used as lixiviant and oxalic acid was used as reductant. The experimental results showed that the manganese and iron separation was optimum when the concentration of the sulfuric acid and oxalic acid were 0.75 M and 30 g/L, respectively, at a temperature of 80 °C, a solid/liquid ratio of 67 g/L, stirring speed of 400 rpm, and leaching duration of 60 min. Under this condition, 90.49% and 6.78% of Mn and Fe were dissolved, respectively, from the ore sample with a size fraction of − 106 μm. It was determined that the leaching of manganese from the ores was a second-order reaction with an activation energy (E<inf>a</inf>) of 53.38 kJ/mol. The leaching residues obtained under the optimum condition were subjected to high-intensity wet magnetic separation tests to recover the remaining iron content. This separation process produced a concentrate containing 56.20% Fe and 1.79% Mn with iron and manganese recoveries of 56.83% and 66.73%, respectively. A magnetic separation test from an unleached ore sample was also carried out as a benchmark. To the best of our knowledge, this is the first time that a magnetic separation process was used to a residue obtained from reductive acid leaching of manganiferous iron ores to recover iron. © 2019, Society for Mining, Metallurgy & Exploration Inc.Article Manganzı Demir Cevherinden Manganın Çözündürülmesinde Farklı İndirgeme Maddelerinin Etkisi(Chamber of Mining Engineers of Turkey, 2022-06-26) Top, S.; Altiner, Mahmut; Kursunoglu, SaitIIn this paper, the manganese extraction from a manganiferous iron ore was investigated using reductive leaching. Various chemicals were used as a reducing agent to leach manganese selectively from the ore in the presence of sulfuric acid (H2SO4) solution. Firstly, optimum dissolution values were determined for selective manganese dissolution without using a reducing agent. As it was aimed at the selective extraction of manganese from the ore, the reductive leaching tests were conducted by adding the reducing agents under the following optimal parameters: a leaching time of 1 h, a stirring speed of 300 rpm, a temperature of 70°C, a sulfuric acid concentration of 1 M where the ore was leached with an extraction ratio of 11.54% Mn and 2.16% Fe. Manganese was dissolved with high efficiencies (up to 97.46%) from the ore by using different organic compounds (tartaric acid (C<inf>4</inf>H<inf>6</inf>O<inf>6</inf>), oxalic acid (C<inf>2</inf>H<inf>2</inf>O<inf>4</inf>), citric acid (C<inf>6</inf>H<inf>8</inf>O<inf>7</inf>), glucose (C<inf>6</inf>H<inf>12</inf>O<inf>6</inf>), sucrose (C<inf>12</inf>H<inf>22</inf>O<inf>11</inf>), and maleic acid (C<inf>4</inf>H<inf>4</inf>O<inf>4</inf>)) as the reducing agents. © 2022 Elsevier B.V., All rights reserved.