Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
3 results
Search Results
Article Comprehensive Evaluation of Microstructure–Property Relationships in Al-Added Sn-Zn Eutectic Solder Alloys from Thermal, Electrical, and Mechanical Perspectives(Springer, 2026) Bayram, Ümit; Şahin, Mevlüt(Sn-8.8Zn)-XAl (X = 0, 0.5, 1.0, 2.5, 5.0 wt.%) solder alloys were produced using a vacuum muffle furnace. The microstructural images, chemical compositions, and phase structures of the alloys were characterized by field emission scanning electron microscopy (FESEM), field emission scanning electron microscopy-energy dispersive x-ray spectroscopy (FESEM-EDX), and x-ray diffraction (XRD) analyses, respectively. According to FESEM images, a fully eutectic microstructure was observed in the Sn-8.8Zn alloy. With increasing Al content, dendritic structures formed and became denser. The mechanical properties of the alloys (ultimate tensile strength sigma UT, tensile yield strength sigma TY, compressive yield strength sigma CY, and Vickers hardness HV) were measured as a function of composition. The highest strength and hardness values were obtained for the (Sn-8.8Zn)-2.5Al alloy, whereas the (Sn-8.8Zn)-5.0Al alloy exhibited the highest ductility. The melting enthalpies (Delta H) and the specific heat differences between the solid and liquid phases (Delta CP) of the alloys were measured by differential scanning calorimetry (DSC) analysis. It was determined that an increase in the Al content of the eutectic alloy resulted in higher measured thermophysical properties. Finally, electrical resistivity (rho) values at T = 300 K, measured using the standard four-point probe method (FPPM), revealed an increase in resistivity up to 1.0 wt.% Al content, followed by a decrease beyond this value. In contrast, thermal conductivity values calculated using the Wiedemann-Franz law exhibited an opposite trend, decreasing up to 1.0 wt.% Al, and increasing thereafter. Based on microstructure-property relationships, the results were compared with previous studies, highlighting that (Sn-8.8Zn)-XAl alloys represent promising alternatives to lead-free solders.Article Tuning Mechanical Performance of PCL Scaffolds: Influence of 3D Bioprinting Parameters, Polymer Concentration, and Solvent Selection(IOP Publishing Ltd, 2025-09-01) Ceylan, Saniye Aylin; Baltacioglu, Mehmet Furkan; Bal, Burak; Bayram, Ferdi Caner; Isoglu, Ismail AlperThe mechanical performance of three-dimensional (3D) bioprinted scaffolds is susceptible to printing parameters and material formulation. In this study, poly (epsilon-caprolactone) (PCL) scaffolds were fabricated using four different polymer concentrations (10%, 25%, 50%, and 75% w/v) to investigate how these variations, along with process parameters, influence mechanical behavior. Maintaining the structural integrity of bioprinted constructs requires careful optimization of polymer concentration and precise control over parameters such as printing speed, pressure, and infill density. Tensile tests were conducted to evaluate the effects of these variables. Among the tested conditions, a 50% (w/v) concentration allowed for a broader operational window, enabling fabrication across a range of printing speeds and pressures. At a printing speed of 5 mm s-1, PCL-DCM exhibited a Young's modulus of 39.0 MPa, while PCL-CF samples printed at 10 mm s-1 achieved the highest modulus of 32.0 MPa. Notably, when the printing speed was kept constant, applying higher pressures led to an increase in Young's modulus, suggesting that pressure plays a key role in enhancing scaffold stiffness. When comparing the 50% and 75% (w/v) polymer concentrations, the 50% (w/v) formulation stood out by offering both higher elongation and greater stiffness, which makes it particularly suitable for load-bearing applications. These findings provide a quantitative framework for optimizing extrusion-based bioprinting of PCL scaffolds, with implications for customized biomedical implants and regenerative medicine.Article Citation - Scopus: 1Ethyl Vinyl Acetate (EVA) Composites With Nanoclays and Boric Acid: Thermal and Mechanical Properties(Turkish Energy, Nuclear and Mining Research Agency, 2025-04-01) Erdem, İlker; Kapçı, Mehmet Fazıl; Avcı, ŞeymaPolimerler pek çok uygulamada kullanılmaktadırlar fakat yanabilir olmaları sorun teşkil etmektedir. Polimerlere yanma dayanımı seramikler gibi (oksitler, hidroksitler, killer, vb.) inorganik malzemeler kullanılarak kazandırılabilir. Bu katkıların ilavesi polimer-inorganik kompozitlerin mekanik özelliklerini de değiştirebilir ki kompozit hazırlamada bu da dikkate alınmalıdır. Bu çalışmada etil vinil asetata (EVA) iki faklı nano-kil (ağırlıkça 20/100 oranına kadar) ve borik asit eklenerek polimerin yanmasında olası gecikme araştırılmıştır. Nano-kil ve BA ilavesinin etkisini belirlemek için saf polimer ve polimer-inorganik kompozitler için mekanik özellikler de belirlenmiştir. Hazırlanan nanokompozitlerin kimyasal yapıları (FT-IR, XRD), ısıl özellikleri (TGA), mekanik özellikleri (çekme testi) ve yanma davranışları değerlendirilmiştir. En yüksek nano-kil içeriğine sahip NC 1.4 örneği en uzun sürede yanmıştır. NC 2 örneğinin diğer örneklerden daha yüksek gerilim dayanımına ve Young katsayısına sahip olduğu bulunmuştur. Nano-killerdeki organik yüzey dönüştürücüler ve BA ilavesi nano-kil/EVA kompozitlerinin ısıl ve mekanik özellikleri üzerinde etkili olmuştur.