Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
2 results
Search Results
Conference Object Citation - Scopus: 2Leaching of Yahyali Non-Sulphide Pb-Zn Flotation Tailing Using Organic Acids(Baski, 2019) Hussaini, Shokrullah; Kursunoglu, Sait; Kaya, MuammerThe laboratory scale leaching of Kayseri-Yahyali non-sulphide lead (Pb)-zinc (Zn) flotation tailing using two organic acids was experimentally investigated. The effect of citric and oxalic acid on the dissolution of Zn, Pb, iron (Fe) and arsenic (As) was individually investigated under the following conditions: citric or oxalic acid concentration of 0.5-1.0M, temperature of 60-80°C and leaching time of 30-180 min. at 1/10 solid-to-liquid (S/L) ratio. 90.1% Zn dissolution was achieved using 0.5 M citric acid at 80°C leaching temperature for 180 min leaching time. The Fe, Pb and As dissolutions were determined as less than 20% under the conditions tested. 95.5% Fe and 68.8% As were removed from the flotation tailing along with less than 5% of Zn and Pb using 1.0 M oxalic acid for 180 min. leaching time at 60°C leaching temperature. It was found that citric acid is more prominent than oxalic acid for the selective leaching of zinc from the flotation tailing whereas a substantial amount of iron and arsenic removal can be achived by oxalic acid leaching. The use of NaCl along with citric acid was not useful for higher Zn dissolution. Based on the experimental results, an appropriate process will be improved for the selective leaching of valuable metals from the Pb-Zn non-sulphide flotation tailing in the near future. © 2020 Elsevier B.V., All rights reserved.Conference Object Citation - Scopus: 2Dissolution of Mixed Zinc-Carbon and Alkaline Battery Powders in Sulphuric Acid Using Ascorbic/Oxalic Acid as a Reductant(Minerals, Metals and Materials Society 184 Thorn Hill Road Warrendale PA 15086, 2012-03-17) Kaya, Muammer; Kursunoglu, SaitThe aim of this study was to investigate the effectiveness of ascorbic (C<inf>6</inf>H<inf>8</inf>O<inf>6</inf>) / oxalic (C<inf>2</inf>H <inf>2</inf>O<inf>4</inf>) acid as a reductant for the simultaneous recovery of zinc and manganese from a spent and mixed zinc-carbon and alkaline battery powder in sulphuric acid leaching. The effects of sulfuric acid concentration, ascorbic/oxalic acid dosages, reaction temperature and leaching time on the zinc and manganese dissolutions were investigated according to 2k full factorial experimental design; then, a simple optimization study was carried out for the best reductant. The optimum reductive acid leaching conditions were determined at 3 hours leaching time, 70°C leaching temperature, 0.5M sulfuric acid concentration, 13 g/L ascorbic acid dosage, 1/20 g/mL solid/liquid ratio and 200 rpm stirring speed. Under these conditions, the dissolution efficiencies were 99.9% for Zn and 99.3% for Mn. When our results were compared with the previous results, our findings were better than previous studies. In addition, the manganese dissolution kinetics was undertaken, and the activation energy was found to be 7.04 kJ/mol. Selective precipitations of Zn and Mn from acid solutions were carried out using NaOH and KOH. Using 3M NaOH as precipitating agent at room temperature and at pH 8; 95.4% of Zn and at pH 10; 93.7% of Mn were precipitated from the leaching solution. Under the same conditions, using 3 M KOH at pH 8; 91.6% of Zn and at pH 10, 96.4% of Mn were precipitated. Based on the experimental results obtained, an appropriate flow sheet was proposed to recover zinc and manganese. © 2020 Elsevier B.V., All rights reserved.