Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
4 results
Search Results
Article Citation - WoS: 10Citation - Scopus: 10Reaction Kinetics and Properties of Pumice-Based Geopolymer Systems Cured at Room Temperature(Elsevier Sci Ltd, 2023-12) Kucukyildirim, Enver; Yorulmaz, Hediye; Durak, Ugur; Ilkentapar, Serhan; Uzal, Burak; Karahan, Okan; Atis, Cengiz DuranThis research investigated the kinetics of pumice-based geopolymer systems and their physical and mechanical properties. The effect of the Na2SiO3/NaOH ratio of geopolymer systems on the rate of heat evolution and total heat of reaction were examined via isothermal calorimetry of geopolymer pastes prepared with Na2SiO3/NaOH ratios of 2.5, 3, and 3.5. Hardened pastes were also studied with thermo-gravimetric analysis to determine weight loss. In addition, the unit weights and compressive strengths of the pastes prepared using pumice were measured. Although the hydration process starts the earliest in pumice-based geopolymer pastes with a Na2SiO3/ NaOH ratio of 2, they have the lowest total hydration temperature. Na2SiO3/NaOH ratio of 2.5 by mass, shows higher weight loss obtained from TGA results. The compressive strength of the paste sample, prepared with a Na2SiO3/NaOH ratio of 3.5 by mass, was the highest, with 36.30 MPa at 28d. Depending on the Na2SiO3/NaOH ratio, it is thought that as the amount of Na2SiO3 increases in the samples, silica gel formation increases in later ages.Article Citation - WoS: 130Citation - Scopus: 140Influence of Admixtures on the Properties of Alkali-Activated Slag Mortars Subjected to Different Curing Conditions(Elsevier Sci Ltd, 2013-02) Bilim, Cahit; Karahan, Okan; Atis, Cengiz Duran; Ilkentapar, SerhanThis paper presents the influence of shrinkage-reducing (SHR) and superplasticizing and set-retarding admixtures (SSRe) on the properties of slag pastes and mortars activated by liquid sodium silicate with different dosage and modulus ratio. Properties in the fresh and hardened state for these binders were investigated by means of measuring some properties including setting time, flowability, flexural strength, compressive strength, carbonation and shrinkage. In this study, fifteen pastes and mortars were prepared. Liquid sodium silicate was used to activate the slag at two sodium concentrations, 4% and 6% by mass of slag. Liquid sodium silicate and sodium hydroxide were blended to obtain 0.75 and 1 modulus ratio of SiO2/Na2O. Results showed that although the higher percentage of sodium in the activator produced a higher strength, workability and setting times rapidly decreased with the higher sodium concentration due to instantaneous reaction and quick hardening of slag activated by liquid sodium silicate. None of the admixtures generally had an impact on the setting times of alkali-activated slag (AAS) pastes. SSRe admixture increased the flow rate of AAS mortars while SHR admixture partially affected the flow values of AAS mortars. SHR admixture exhibited a slight decrease in the carbonation depths of AAS mortars. SSRe and particularly SHR chemical admixtures reduced the shrinkage of AAS mortars. However, the shrinkage values of AAS mortars still were higher than those of ordinary Portland cement (NPC) mortars. Curing conditions had a significant effect on the mechanical behavior in the hardened state of AAS mortars compared to NPC mortars. (C) 2012 Elsevier Ltd. All rights reserved.Article Citation - WoS: 10Citation - Scopus: 10Characterizing Boron-Enhanced One-Part Alkaline-Activated Mortars: Mechanical Properties, Microstructure and Environmental Impacts(Elsevier Sci Ltd, 2024-05) Orklemez, Ezgi; Ilkentapar, Serhan; Durak, Ugur; Gulcimen, Sedat; Uzal, Nigmet; Uzal, Burak; Atis, Cengiz DuranSince alkali activators negatively effect the environmental impact assessment, it is necessary to develop the alternative activators from natural sources with low environmental impact. Therefore, in this study, the usage of boron refined products colemanite, ulexite and boron pentahydrate as activators in slag-based alkali-activated mortar systems was investigated in detail. Flexural and compressive strength tests, isothermal calorimetry measurement, thermogravimetric and differential thermal analysis, inductively coupled plasma mass spectrometry analysis, field emission scanning electron microscopy, and energy dispersive analysis and elemental mapping and X-ray diffraction analysis were carried out on the samples. In addition, sample production was subjected to life cycle analysis (LCA) with a cradle-to-gate approach using two different transportation scenarios. According to the results obtained, it was determined that colemanite, ulexite and boron penta hydrate, when used in optimum proportions, had a positive effect on strength (up to increase 40% compressive strength by 20% ulexite replacement) and could be used as an activator in slag-based alkali-activated systems. The positive results obtained in strength as a result of using boron-refined products are also supported by other test results conducted within the scope of the study. Furthermore, according to the LCA results, it was observed that there was a significant decrease in global warming potential with the substitution of 20% colemanite, ulexite or boron pentahydrate as activators, not only compared to the reference sample but also traditional cementitious systems.Article Citation - WoS: 36Citation - Scopus: 40A New Parameter Influencing the Reaction Kinetics and Properties of Fly Ash Based Geopolymers: A Pre-Rest Period Before Heat Curing(Elsevier, 2021-03) Durak, Ugur; Ilkentapar, Serhan; Karahan, Okan; Uzal, Burak; Atis, Cengiz DuranIn this study, the influence of a pre-rest period before heat curing (as a new parameter), on the physical properties, flexural and compressive strength, and microstructure of geopolymer mortars and pastes produced with alkali activation of fly ash were investigated. In this context, geopolymer mortar and paste samples were prepared and pre-rested under laboratory conditions for 0, 1, 2, 3, 7, 14, and 28 days before heat curing. After the pre-rest period, the samples were subjected to heat curing at 75 degrees C in an oven, for 2 days. Mortar and paste samples exposed to a pre-rest period while in the fresh state before heat curing were compared with control samples without pre-resting. Water absorption, porosity, specific gravity, capillarity, flexural strength, compressive strength, and abrasion resistance tests were conducted on the geopolymer mortar samples. A reaction kinetics study using an isothermal calorimeter, XRD, and SEM analyses were performed on the geopolymer paste samples for microstructural investigations. Based on the results obtained, it was observed that the mechanical strength of the samples subjected to the pre-rest period before heat curing increased considerably compared to the reference (without pre-resting) samples. In addition, because of pre-resting, the capillarity coefficient, water permeability, and porosity of the samples decreased compared to the reference samples, and it was concluded that pre-resting improves durability-related properties. Moreover, the reaction kinetics and SEM analysis results, supporting the above findings, showed that a pre-resting period increases the geopolymeric reaction products and causes a denser microstructure.