Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
3 results
Search Results
Correction Citation - WoS: 2Citation - Scopus: 2The Influence of Cement Kiln Dust on Strength and Durability Properties of Cement-Based Systems(Springer Heidelberg, 2022-06-15) Hakkomaz, Hadiye; Yorulmaz, Hediye; Durak, Ugur; Ilkentapar, Serhan; Karahan, Okan; Atis, Cengiz DuranArticle Citation - WoS: 7Citation - Scopus: 7The Influence of Cement Kiln Dust on Strength and Durability Properties of Cement-Based Systems(Springer Heidelberg, 2022-06-06) Hakkomaz, Hadiye; Yorulmaz, Hediye; Durak, Ugur; Ilkentapar, Serhan; Karahan, Okan; Atis, Cengiz DuranThere are very few studies in the literature on the usage of CKD in cementitious systems. This article presents the laboratory study results on the influence of cement kiln dust (CKD) on the properties of mortar made with cement kiln dust and Portland cement. The article aims to prevent CKD's (known as a hazardous waste product) damage to nature by utilizing CKD in cementitious systems and contributing to sustainability by reducing cement amount in the cementitious system. For this purpose, 5%, 10%, 15%, and 20% of CKD were replaced with cement and binary cementitious systems were formed. For all mortar mixes, the water/binder ratio was kept constant at 0.5, and the sand/binder ratio was 3. Workability, dry unit weight, water absorption ratio and porosity, flexural strength, compressive strength, abrasion, carbonation, and high-temperature resistance tests were performed on the mortar specimens. Based on the results of laboratory work, it was observed that the replacement of CKD with cement reduces the workability of fresh mortar. Compressive and flexural strengths of CKD-added mixtures were found to be equivalent or insignificantly lower than that of the control sample. The addition of CKD had a negligible effect on water absorption and porosity of samples. Besides, the residual compressive strength determined after the elevated temperature test for the sample made with CKD were found to be equivalent or higher compared to the control sample. Present laboratory studies showed that utilization of CKD in cementitious mortar system is feasible in terms of testing conducted.Article Citation - WoS: 6Citation - Scopus: 8The Effects of Different Types of Fly Ash on the Compressive Strength Properties of Briquettes(Hindawi Ltd, 2011) Sola, Ozlem Celik; Yayla, Murat; Sayin, Baris; Atis, Cengiz Duran; Duran Atiş, Cengiz; Sayin, Bariş; Sayın, BarişThe aim of this study is to evaluate the effect of the different types of fly ash on the compressive strength properties of sintered briquettes. Thermal gravimetric (TG) analysis was carried out. The chemical composition and physical properties of the materials used were determined. Particle size distribution and microstructure elemental analyses of the materials used were carried out by a particle size analyzer (Mastersizer) and a scanning electron microscope (SEM-EDS). Following the characterization of the materials, briquettes were prepared by sintering at different temperatures. Compressive strength test results of the briquette samples indicated that briquettes with a compressive strength value of 47.45 N/mm(2) can be produced. The results obtained exceed the Turkish standard (TS EN 771-1) requirements (9.8-23.54 N/mm(2)). SEM-EDS results showed that briquette samples made with Tuncbilek (T) fly ash had a higher percentage of the glassy phase than the other briquette samples. Due to this microstructure, it results in higher compressive strength value.