Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
3 results
Search Results
Article Citation - WoS: 76Citation - Scopus: 81Influence of NaNo SiO2 and NaNo CaCo3 Particles on Strength, Workability, and Microstructural Properties of Fly Ash-Based Geopolymer(Ernst & Sohn, 2020-05-06) Durak, Ugur; Karahan, Okan; Uzal, Burak; Ilkentapar, Serhan; Atis, Cengiz DuranThe influence of nano SiO2(NS) and CaCO3(NC) particles on the properties of class F fly ash based geopolymer mortar activated with different sodium ion concentrations have been investigated. Mortar mixture proportions were 1:3:0.3 for binder, sand, and water, respectively. Nano SiO2 and CaCO3 particles were replaced with a binder by weight basis at the ratios of 1, 2, and 3% in the mixtures. Sodium concentrations amount used were 8, 10, and 12% Na+ of binder content. Geopolymer mortar samples were cured at 60, 75, and 90 degrees C in a furnace for 24, 48, and 72 hr. After the heat curing process, flexural, and compressive strength tests were performed. The changes in the microstructure of geopolymer due to influence of nanoparticles were examined by utilizing isothermal calorimetric studies on geopolymer paste, and field-emission scanning electron microscopy (FESEM). Based on laboratory work results, it was concluded that for all sodium ion concentrations, the addition of nano SiO2 and CaCO3 particles improved the flexural and compressive strengths after 24 hr heat curing. However, the favorable effects of nanoparticles on strength properties tend to disappear after 48 and 72 hr heat curing. The results of isothermal calorimetric studies showed that nano SiO2 and CaCO3 particles accelerated the geopolymeric reactions at an early age. FESEM results showed that additions of nanoparticles made the microstructure of geopolymer products more intense and compact.Article Citation - WoS: 9Citation - Scopus: 11Evaluation of Diatomite Substitute With Thermal Power Plant Waste Fly Ash in Sustainable Geopolymer Through Life Cycle Assessment(Springer, 2025-02-28) Ilkentapar, Serhan; Orklemez, Ezgi; Durak, Ugur; Gulcimen, Sedat; Bayram, Savas; Uzal, Nigmet; Atis, Cengiz DuranThis research demonstrates the potential of diatomite as a fly ash replacement to improve mechanical properties and environmental sustainability and presents it as a viable alternative for sustainable construction. Additionally, a life cycle assessment (LCA) was conducted on the produced mortars to quantitatively compare their environmental impacts using a cradle-to-gate approach. In mixtures, it was used by replacing the diatomite in the ratios of 1%, 2%, 3%, 4%, and 5% by weight of the fly ash. Workability, unit weight, flexural and compressive strength, abrasion resistance, elevated temperature resistance and microstructure analysis were carried out. The results indicated that replacing 1%, 2%, and 3% diatomite increased the compressive and flexural strength of mortars due to their higher specific surface area. Two percent replacement of diatomite provided the best results. FESEM results of 3% diatomite inclusion showed more intense and compact microstructure of geopolymer. Diatomite inclusion increased the abrasion resistance of geopolymer. Since 2% diatomite replacement was found to be optimum, the LCA results showed that geopolymer mortar with 2% diatomite has 25% lower impacts in terms of global warming potential and 10% lower impacts in terms of terrestrial ecotoxicity than conventional Portland cement mortar.Article Citation - WoS: 32Citation - Scopus: 35A New Parameter Influencing the Reaction Kinetics and Properties of Fly Ash Based Geopolymers: A Pre-Rest Period Before Heat Curing(Elsevier, 2021-03) Durak, Ugur; Ilkentapar, Serhan; Karahan, Okan; Uzal, Burak; Atis, Cengiz DuranIn this study, the influence of a pre-rest period before heat curing (as a new parameter), on the physical properties, flexural and compressive strength, and microstructure of geopolymer mortars and pastes produced with alkali activation of fly ash were investigated. In this context, geopolymer mortar and paste samples were prepared and pre-rested under laboratory conditions for 0, 1, 2, 3, 7, 14, and 28 days before heat curing. After the pre-rest period, the samples were subjected to heat curing at 75 degrees C in an oven, for 2 days. Mortar and paste samples exposed to a pre-rest period while in the fresh state before heat curing were compared with control samples without pre-resting. Water absorption, porosity, specific gravity, capillarity, flexural strength, compressive strength, and abrasion resistance tests were conducted on the geopolymer mortar samples. A reaction kinetics study using an isothermal calorimeter, XRD, and SEM analyses were performed on the geopolymer paste samples for microstructural investigations. Based on the results obtained, it was observed that the mechanical strength of the samples subjected to the pre-rest period before heat curing increased considerably compared to the reference (without pre-resting) samples. In addition, because of pre-resting, the capillarity coefficient, water permeability, and porosity of the samples decreased compared to the reference samples, and it was concluded that pre-resting improves durability-related properties. Moreover, the reaction kinetics and SEM analysis results, supporting the above findings, showed that a pre-resting period increases the geopolymeric reaction products and causes a denser microstructure.