Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
3 results
Search Results
Article Citation - WoS: 2Citation - Scopus: 2A Novel Biomass-Derived Reductant for Nitric Acid Dissolution of Manganiferous Iron Ore: Comparative Assessment of Organic Reductants(MDPI, 2025-12-31) Top, Soner; Altiner, Mahmut; Vapur, Huseyin; Kursunoglu, Sait; Stopic, SreckoThis study investigates the selective dissolution of manganese from a manganiferous iron ore using nitric acid (HNO3) in the presence of various organic reductants. A series of leaching experiments was performed to evaluate the effects of temperature, reductant type, and leaching time on Mn recovery, with particular emphasis on biomass (horse dung) and tartaric acid as novel reducing agents. The dissolution behaviour of Fe, Mn, Mg, Ca, and Al was systematically examined, revealing that Mn extraction was strongly enhanced in the presence of reductants, while Fe dissolution remained below 10% under all conditions. The maximum Mn dissolution exceeded 90% at 90 degrees C using biomass and reached nearly 85%-90% with tartaric acid at elevated temperatures. Kinetic studies were conducted by applying reaction order models and the shrinking core model. The results indicated that Mn dissolution in HNO3 medium is predominantly controlled by surface chemical reaction, with Arrhenius analysis yielding activation energies of 27.74 kJ/mol for biomass and 21.26 kJ/mol for tartaric acid. These relatively low values confirm the efficiency of organic reductants in facilitating Mn reduction and dissolution. To sum up, comparison of reductant efficiency revealed that, at the lowest concentrations, the dissolution of Mn followed the sequence glucose > sucrose > oxalic acid > tartaric acid > maleic acid > biomass > citric acid > acetic acid. At the highest concentrations, the trend shifted, with citric acid emerging as the most effective, followed by tartaric acid > oxalic acid > glucose > sucrose > maleic acid > biomass > acetic acid.Article Manganzı Demir Cevherinden Manganın Çözündürülmesinde Farklı İndirgeme Maddelerinin Etkisi(Chamber of Mining Engineers of Turkey, 2022-06-26) Top, S.; Altiner, Mahmut; Kursunoglu, SaitIIn this paper, the manganese extraction from a manganiferous iron ore was investigated using reductive leaching. Various chemicals were used as a reducing agent to leach manganese selectively from the ore in the presence of sulfuric acid (H2SO4) solution. Firstly, optimum dissolution values were determined for selective manganese dissolution without using a reducing agent. As it was aimed at the selective extraction of manganese from the ore, the reductive leaching tests were conducted by adding the reducing agents under the following optimal parameters: a leaching time of 1 h, a stirring speed of 300 rpm, a temperature of 70°C, a sulfuric acid concentration of 1 M where the ore was leached with an extraction ratio of 11.54% Mn and 2.16% Fe. Manganese was dissolved with high efficiencies (up to 97.46%) from the ore by using different organic compounds (tartaric acid (C<inf>4</inf>H<inf>6</inf>O<inf>6</inf>), oxalic acid (C<inf>2</inf>H<inf>2</inf>O<inf>4</inf>), citric acid (C<inf>6</inf>H<inf>8</inf>O<inf>7</inf>), glucose (C<inf>6</inf>H<inf>12</inf>O<inf>6</inf>), sucrose (C<inf>12</inf>H<inf>22</inf>O<inf>11</inf>), and maleic acid (C<inf>4</inf>H<inf>4</inf>O<inf>4</inf>)) as the reducing agents. © 2022 Elsevier B.V., All rights reserved.Article Citation - Scopus: 6Extraction of Lanthanum and Cerıum from a Bastnasite Ore By Direct Acidic Leaching(Chamber of Mining Engineers of Turkey, 2020-06-01) Kursunoglu, Sait; Top, S.; Hussaini, Shokrullah; Gokcen, H. S.; Altiner, Mahmut; Ozsarac, Safak; Kaya, MuammerThe extraction of lanthanum (La) and cerium (Ce) from a bastnasite ore by direct acidic leaching was investigated. The effects of acid concentration and leaching temperature on the extraction of La and Ce from the ore were tested. Using nitric (NHO3), more than 85% of the La and Ce were simultaneously extracted into leach solution whereas the La and Ce dissolutions were determined as less than 85% by using sulfuric acid (H2SO4). The La dissolution exceeded 90% by using hydrochloric acid (HCl); however, the Ce dissolution remained below 85% under the following conditions: solid-to-liquid ratio of 20% (w/v), the acid concentration of 20%, leaching temperature of 25°C and leaching time of 1 h. The result revealed that HNO3 could be used as a solvent for the maximum simultaneous extraction of the La and Ce from the bastnasite ore. The leaching temperature had no crucial effect on the dissolution of La and Ce when HNO3 or HCl solutions were preferred as a solvating agent. However, the leaching temperature had a slight positive effect on the dissolutions of La and Ce when H2SO4 was used as a solvent. © 2023 Elsevier B.V., All rights reserved.