Scopus İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/395
Browse
2 results
Search Results
Article Raster Orientation Effects on the Adhesion of iCVD-Deposited PSA Thin Films on FDM-Printed PLA(MDPI, 2026-01-30) Yilmaz, Kurtulus; Gursoy, Mehmet; Gunes, Aydin; Karaman, MustafaThe adhesion performance of pressure-sensitive adhesive (PSA) thin films on additively manufactured polymers is strongly governed by surface anisotropy induced during printing. In this study, PSA thin films based on 2-ethylhexyl acrylate (EHA) and acrylic acid (AA) were deposited by initiated chemical vapor deposition (iCVD) onto fused deposition modeling (FDM) printed PLA substrates with different raster orientations (0 degrees, 30 degrees, 60 degrees, and 90 degrees). The deposited films exhibited high optical transparency on glass, and thicknesses consistent with the targeted deposition. Adhesion performance was evaluated using tensile and three-point bending tests, revealing a strong dependence on raster orientation. The 0 degrees raster orientation yielded the highest shear adhesion strengths, reaching 12.03 N/cm2 under tensile loading and 4.59 N/cm2 under bending, along with the largest failure displacements. In contrast, specimens printed at 90 degrees exhibited an approximately 47% reduction in tensile shear adhesion strength and limited deformation prior to failure. SEM analysis showed that raster alignment parallel to the loading direction promoted extensive adhesive deformation and PSA fibrillation, whereas higher raster angles resulted in predominantly interfacial debonding. These results demonstrate that raster orientation is a critical design parameter for tuning PSA adhesion on FDM-printed PLA substrates without modifying adhesive chemistry.Article Citation - WoS: 6Citation - Scopus: 6Experimental and Statistical Damage Analysis in Milling of S2-Glass Fiber/Epoxy and Basalt Fiber/Epoxy Composites(Wiley, 2024-07-30) Sayin, Ahmed Cagri; Danisman, Sengul; Ersoy, Emin; Yilmaz, Cagatay; Kesriklioglu, SinanS2-glass fiber reinforced plastics (S2-GFRP) and basalt fiber reinforced plastics (BFRP) have emerged as crucial materials due to their exceptional mechanical properties, and milling of composite materials plays an important role in achieving desired properties. However, they have proven challenges due to relative inhomogeneity compared with metals, resulting unpredictability in quality of milling operations. The objective of this work is to investigate the effect of cutting parameters, tool geometry and tool surface materials on the surface quality of composites using burrs as a metric. S2-GFRP and BFRP composites were produced by the vacuum infusion method. Helical and straight flute end mills were manufactured from high-speed steel (HSS) and carbide rounds, and half of them were coated with titanium nitride using reactive magnetron sputtering technique. Taguchi L18 orthogonal array is used to determine the effect of tool material, tool angle, coating, cutting direction, spindle speed, and feed rate on the machining quality of S2-GFRPs and BFRPs with respect to burr formations. Milling experiments were conducted under dry conditions and then the burrs were imaged to calculate the total area and length. Statistical analysis was also performed to optimize the machining parameters and tool type for ensuring the structural integrity and performance of the final composite parts. The results showed that the selection of tool material has the most significant impact on the burr area and length of the machined surface. The novel image analysis allows to analyze the extent of the burr size with a desirable operation speed for industrial applications.