WoS İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/394
Browse
2 results
Search Results
Article Citation - WoS: 16Citation - Scopus: 19Recovery of Zinc and Lead from Yahyali Non-Sulphide Flotation Tailing by Sequential Acidic and Sodium Hydroxide Leaching in the Presence of Potassium Sodium Tartrate(Elsevier, 2020-12) Kursunoglu, Sait; Top, Soner; Kaya, MuammerThe recovery of zinc and lead from Yahyali non-sulphide flotation tailing using sulfuric acid followed by sodium hydroxide leaching in the presence of potassium sodium tartrate was experimentally investigated. In the acidic leaching stage, the effects of pH, solid-to-liquid ratio and temperature on the dissolution of zinc from the tailing were explored. 82.3% Zn dissolution was achieved at a pH of 2, a temperature of 40 degrees C, a solid-to-liquid ratio of 20% and a leaching time of 2 h, whereas the iron and lead dissolutions were determined to be less than 0.5%. The sulfuric acid consumption was found to be 110.6 kg/t (dry tailing). The leaching temperature had no beneficial effect on the dissolution of zinc from the tailing. The acidic leach solution was subjected to an electrowinning test. The cathode product consisted of 99.8% Zn and 0.15% Fe. In the alkaline leaching stage, the Pb dissolution increased slightly in the presence of potassium sodium tartrate. More than 60% of Pb was taken into the leach solution when the leaching temperature increased from 40 to 80 degrees C. The final leach residue was analyzed by XRD and XRF. The XRD results indicated that the major peaks originated from the goethite and quartz while minor peaks stem from smithsonite and cemssite. The XRF analysis demonstrated that the residue contained 70.3% iron oxide. Based on the sequential leaching experiments, the zinc and lead were excellently depleted from the flotation tailing, leaving a considerable amount of iron in the final residue.Article Citation - WoS: 14Citation - Scopus: 18Pb-Zn Recovery From a Malic Leach Solution of a Carbonate Type Ore Flotation Tailing by Precipitation and Solvent Extraction(Elsevier, 2021-10) Hussaini, Shokrullah; Tita, Angela Manka; Kursunoglu, Sait; Top, Soner; Ichlas, Zela Tanlega; Kar, Umut; Kaya, MuammerThe recovery of zinc and lead from a malic leach solution of a carbonate type ore flotation tailing by precipitation with sulfuric acid followed by solvent extraction using di(2-ethylhexyl)phosphoric acid (D2EHPA) as extractant was investigated. The separation of lead via precipitation was essentially complete from the malic acid leach solution by adding sulphuric acid to reach a pH of 0.25 at 25 degrees C. The precipitate product was identified by XRD as anglesite (PbSO4). The pregnant leach solution after lead precipitation was then subjected to solvent extraction using D2EHPA. The optimum solvent extraction conditions were determined as 10% D2EHPA concentration, 25 degrees C temperature, 10 min contact time and phase ratio of unity. Under these conditions, 99.3% of zinc was extracted into the organic phase at a pH of 4.2 in a single contact alongside a substantial amount of Ca (76.6%), and minor amounts of Fe (19.2%) and Mg (18%). Complete stripping of zinc and calcium from the loaded organic solution along with 47.8% of Mg was achieved at a pH 0.5 under room temperature. No iron stripping was observed from the loaded organic. The zinc content in the loaded strip solution could be enriched and then sent to the electrowinning (EW) stage. It is noted that the calcium and magnesium impurities in the loaded strip solution had no adverse effect on the zinc EW process. Based on the experimental results, a flowsheet was proposed for the recovery of Pb and Zn from the malic acid leach solution. With the proposed precipitation and solvent extraction process, two different material streams are produced.