WoS İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/394
Browse
2 results
Search Results
Article Tuning Mechanical Performance of PCL Scaffolds: Influence of 3D Bioprinting Parameters, Polymer Concentration, and Solvent Selection(IOP Publishing Ltd, 2025-09-01) Ceylan, Saniye Aylin; Baltacioglu, Mehmet Furkan; Bal, Burak; Bayram, Ferdi Caner; Isoglu, Ismail AlperThe mechanical performance of three-dimensional (3D) bioprinted scaffolds is susceptible to printing parameters and material formulation. In this study, poly (epsilon-caprolactone) (PCL) scaffolds were fabricated using four different polymer concentrations (10%, 25%, 50%, and 75% w/v) to investigate how these variations, along with process parameters, influence mechanical behavior. Maintaining the structural integrity of bioprinted constructs requires careful optimization of polymer concentration and precise control over parameters such as printing speed, pressure, and infill density. Tensile tests were conducted to evaluate the effects of these variables. Among the tested conditions, a 50% (w/v) concentration allowed for a broader operational window, enabling fabrication across a range of printing speeds and pressures. At a printing speed of 5 mm s-1, PCL-DCM exhibited a Young's modulus of 39.0 MPa, while PCL-CF samples printed at 10 mm s-1 achieved the highest modulus of 32.0 MPa. Notably, when the printing speed was kept constant, applying higher pressures led to an increase in Young's modulus, suggesting that pressure plays a key role in enhancing scaffold stiffness. When comparing the 50% and 75% (w/v) polymer concentrations, the 50% (w/v) formulation stood out by offering both higher elongation and greater stiffness, which makes it particularly suitable for load-bearing applications. These findings provide a quantitative framework for optimizing extrusion-based bioprinting of PCL scaffolds, with implications for customized biomedical implants and regenerative medicine.Article Citation - WoS: 14Citation - Scopus: 15Lateral Angular Co-Extrusion: Geometrical and Mechanical Properties of Compound Profiles(MDPI, 2020-08-28) Thuerer, Susanne Elisabeth; Peddinghaus, Julius; Heimes, Norman; Bayram, Ferdi Caner; Bal, Burak; Uhe, Johanna; Klose, Christian; Thürer, Susanne ElisabethA novel co-extrusion process for the production of coaxially reinforced hollow profiles has been developed. Using this process, hybrid hollow profiles made of the aluminum alloy EN AW-6082 and the case-hardening steel 20MnCr5 (AISI 5120) were produced, which can be forged into hybrid bearing bushings by subsequent die forging. For the purpose of co-extrusion, a modular tooling concept was developed where steel tubes made of 20MnCr5 are fed laterally into the tool. This LACE (lateral angular co-extrusion) process allows for a variation of the volume fraction of the reinforcement by using steel tubes with different wall thicknesses, which enabled the production of compound profiles having reinforcement contents of either 14 vol.% or 34 vol.%. The shear strength of the bonding area of these samples was determined in push-out tests. Additionally, mechanical testing of segments of the hybrid profiles using shear compression tests was employed to provide information about the influence of different bonding mechanisms on the strength of the composite zone.