PubMed İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12573/397
Browse
3 results
Search Results
Article Raster Orientation Effects on the Adhesion of iCVD-Deposited PSA Thin Films on FDM-Printed PLA(MDPI, 2026-01-30) Yilmaz, Kurtulus; Gursoy, Mehmet; Gunes, Aydin; Karaman, MustafaThe adhesion performance of pressure-sensitive adhesive (PSA) thin films on additively manufactured polymers is strongly governed by surface anisotropy induced during printing. In this study, PSA thin films based on 2-ethylhexyl acrylate (EHA) and acrylic acid (AA) were deposited by initiated chemical vapor deposition (iCVD) onto fused deposition modeling (FDM) printed PLA substrates with different raster orientations (0 degrees, 30 degrees, 60 degrees, and 90 degrees). The deposited films exhibited high optical transparency on glass, and thicknesses consistent with the targeted deposition. Adhesion performance was evaluated using tensile and three-point bending tests, revealing a strong dependence on raster orientation. The 0 degrees raster orientation yielded the highest shear adhesion strengths, reaching 12.03 N/cm2 under tensile loading and 4.59 N/cm2 under bending, along with the largest failure displacements. In contrast, specimens printed at 90 degrees exhibited an approximately 47% reduction in tensile shear adhesion strength and limited deformation prior to failure. SEM analysis showed that raster alignment parallel to the loading direction promoted extensive adhesive deformation and PSA fibrillation, whereas higher raster angles resulted in predominantly interfacial debonding. These results demonstrate that raster orientation is a critical design parameter for tuning PSA adhesion on FDM-printed PLA substrates without modifying adhesive chemistry.Article Citation - WoS: 11Citation - Scopus: 12Towards Analysis and Optimization for Contact Zone Temperature Changes and Specific Wear Rate of Metal Matrix Composite Materials Produced From Recycled Waste(MDPI, 2021-09-08) Gunes, Aydin; Salur, Emin; Aslan, Abdullah; Kuntoglu, Mustafa; Giasin, Khaled; Pimenov, Danil Yurievich; Sahin, Omer SinanTribological properties are important to evaluate the in-service conditions of machine elements, especially those which work as tandem parts. Considering their wide range of application areas, metal matrix composites (MMCs) serve as one of the most significant materials equipped with desired mechanical properties such as strength, density, and lightness according to the place of use. Therefore, it is crucial to determine the wear performance of these materials to obtain a longer life and to overcome the possible structural problems which emerge during the production process. In this paper, extensive discussion and evaluation of the tribological performance of newly produced spheroidal graphite cast iron-reinforced (GGG-40) tin bronze (CuSn10) MMCs, including optimization, statistical, graphical, and microstructural analysis for contact zone temperature and specific wear rate, are presented. For this purpose, two levels of production temperature (400 and 450 degrees C), three levels of pressure (480, 640, and 820 MPa), and seven different samples reinforced by several ingredients (from 0 to 40 wt% GGG-40, pure CuSn10, and GGG-40) were investigated. According to the obtained statistical results, the reinforcement ratio is remarkably more effective on contact zone temperature and specific wear rate than temperature and pressure. A pure CuSn10 sample is the most suitable option for contact zone temperature, while pure GGG-40 seems the most suitable material for specific wear rates according to the optimization results. These results reveal the importance of reinforcement for better mechanical properties and tribological performance in measuring the capability of MMCs.Article Citation - WoS: 18Citation - Scopus: 21Optimization Study on Surface Roughness and Tribological Behavior of Recycled Cast Iron Reinforced Bronze MMCs Produced by Hot Pressing(MDPI, 2021-06-17) Gunes, Aydin; Sahin, Omer Sinan; Duzcukoglu, Hayrettin; Salur, Emin; Aslan, Abdullah; Kuntoglu, Mustafa; Pimenov, Danil YurievichSurface roughness reflects the quality of many operational parameters, namely service life, wear characteristics, working performance and tribological behavior of the produced part. Therefore, tribological performance is critical for the components used as tandem parts, especially for the MMCs (Metal Matrix Composites) which are a unique class of materials having extensive application areas such as aerospace, aeronautics, marine engineering and the defense industry. Current work covers the optimization study of production parameters for surface roughness and tribological indicators of newly produced cast iron reinforced bronze MMCs. In this context, two levels of temperature (400 and 450 degrees C), three levels of pressure (480, 640 and 820 MPa) and seven levels of reinforcement ratios (60/40, 70/30, 80/20, 90/10, 100/0 of GGG40/CuSn10, pure bronze-as received and pure cast iron-as received) are considered. According to the findings obtained by Taguchi's signal-to-noise ratios, the reinforcement ratio has a dominant effect on surface roughness parameters (Ra and Rz), the coefficient of friction and the weight loss in different levels. In addition, 100/0 reinforced GGG40/CuSn10 gives minimum surface roughness, pure cast iron provides the best weight loss and pure bronze offers the desired coefficient of friction. The results showed the importance of material ingredients on mechanical properties by comparing a wide range of samples from starting the production phase, which provides a perspective for manufacturers to meet the market supply as per human requirements.