Characterizing Boron-Enhanced One-Part Alkaline-Activated Mortars: Mechanical Properties, Microstructure and Environmental Impacts
(Elsevier Sci Ltd, 2024) Orklemez, Ezgi; Ilkentapar, Serhan; Durak, Ugur; Gulcimen, Sedat; Uzal, Nigmet; Uzal, Burak; Atis, Cengiz Duran
Since alkali activators negatively effect the environmental impact assessment, it is necessary to develop the alternative activators from natural sources with low environmental impact. Therefore, in this study, the usage of boron refined products colemanite, ulexite and boron pentahydrate as activators in slag-based alkali-activated mortar systems was investigated in detail. Flexural and compressive strength tests, isothermal calorimetry measurement, thermogravimetric and differential thermal analysis, inductively coupled plasma mass spectrometry analysis, field emission scanning electron microscopy, and energy dispersive analysis and elemental mapping and X-ray diffraction analysis were carried out on the samples. In addition, sample production was subjected to life cycle analysis (LCA) with a cradle-to-gate approach using two different transportation scenarios. According to the results obtained, it was determined that colemanite, ulexite and boron penta hydrate, when used in optimum proportions, had a positive effect on strength (up to increase 40% compressive strength by 20% ulexite replacement) and could be used as an activator in slag-based alkali-activated systems. The positive results obtained in strength as a result of using boron-refined products are also supported by other test results conducted within the scope of the study. Furthermore, according to the LCA results, it was observed that there was a significant decrease in global warming potential with the substitution of 20% colemanite, ulexite or boron pentahydrate as activators, not only compared to the reference sample but also traditional cementitious systems.
Citation - WoS: 6
Citation - Scopus: 7
Evaluation of Diatomite Substitute With Thermal Power Plant Waste Fly Ash in Sustainable Geopolymer Through Life Cycle Assessment
(Springer, 2025) Ilkentapar, Serhan; Orklemez, Ezgi; Durak, Ugur; Gulcimen, Sedat; Bayram, Savas; Uzal, Nigmet; Atis, Cengiz Duran
This research demonstrates the potential of diatomite as a fly ash replacement to improve mechanical properties and environmental sustainability and presents it as a viable alternative for sustainable construction. Additionally, a life cycle assessment (LCA) was conducted on the produced mortars to quantitatively compare their environmental impacts using a cradle-to-gate approach. In mixtures, it was used by replacing the diatomite in the ratios of 1%, 2%, 3%, 4%, and 5% by weight of the fly ash. Workability, unit weight, flexural and compressive strength, abrasion resistance, elevated temperature resistance and microstructure analysis were carried out. The results indicated that replacing 1%, 2%, and 3% diatomite increased the compressive and flexural strength of mortars due to their higher specific surface area. Two percent replacement of diatomite provided the best results. FESEM results of 3% diatomite inclusion showed more intense and compact microstructure of geopolymer. Diatomite inclusion increased the abrasion resistance of geopolymer. Since 2% diatomite replacement was found to be optimum, the LCA results showed that geopolymer mortar with 2% diatomite has 25% lower impacts in terms of global warming potential and 10% lower impacts in terms of terrestrial ecotoxicity than conventional Portland cement mortar.