Effect of Nano-SiO2 on Strength and Hydration Characteristics of Ternary Cementitious Systems
(Springer Heidelberg, 2023) Yorulmaz, Hediye; Uzal, Burak; Karahan, Okan; Durak, Ugur; Ilkentapar, Serhan; Atis, Cengiz Duran
This paper shows results of laboratory study on the effects of nano-SiO2 on Portland cement-fly ash systems. It is aimed to improve performance of fly ash-cement systems, particularly at early age, with the inclusion of nano-SiO2. In order to observe the effects of nano-SiO2 particles on the strength and hydration kinetics of fly ash blended cementitious systems, binary and ternary systems were prepared by adding 0.25-1.5% nano-SiO2 by weight of blended cements. Workability, setting time, water absorption capacity, fire resistance, compressive strength and isothermal calorimeter tests were conducted on the cementitious systems. The results indicate that increasing quantity of fly ash increased workability, setting time, water absorption capacity of cementitious systems, whereas the increasing quantity of nano-SiO2 reduced these values. Significant increment in compressive strength were observed, especially at early ages of fly ash-cement systems with nano-SiO2 addition, compared to fly ash added systems, which may compensate for the decrease in compressive strength caused by fly ash. Nano-SiO2 addition accelerated hydration reactions at early age. By partially eliminating the negative effects of fly ash with nano-SiO2, high rates of fly ash can be used in cementitious systems, thus forming more sustainable systems.
Citation - WoS: 6
Citation - Scopus: 6
Characterizing Boron-Enhanced One-Part Alkaline-Activated Mortars: Mechanical Properties, Microstructure and Environmental Impacts
(Elsevier Sci Ltd, 2024) Orklemez, Ezgi; Ilkentapar, Serhan; Durak, Ugur; Gulcimen, Sedat; Uzal, Nigmet; Uzal, Burak; Atis, Cengiz Duran
Since alkali activators negatively effect the environmental impact assessment, it is necessary to develop the alternative activators from natural sources with low environmental impact. Therefore, in this study, the usage of boron refined products colemanite, ulexite and boron pentahydrate as activators in slag-based alkali-activated mortar systems was investigated in detail. Flexural and compressive strength tests, isothermal calorimetry measurement, thermogravimetric and differential thermal analysis, inductively coupled plasma mass spectrometry analysis, field emission scanning electron microscopy, and energy dispersive analysis and elemental mapping and X-ray diffraction analysis were carried out on the samples. In addition, sample production was subjected to life cycle analysis (LCA) with a cradle-to-gate approach using two different transportation scenarios. According to the results obtained, it was determined that colemanite, ulexite and boron penta hydrate, when used in optimum proportions, had a positive effect on strength (up to increase 40% compressive strength by 20% ulexite replacement) and could be used as an activator in slag-based alkali-activated systems. The positive results obtained in strength as a result of using boron-refined products are also supported by other test results conducted within the scope of the study. Furthermore, according to the LCA results, it was observed that there was a significant decrease in global warming potential with the substitution of 20% colemanite, ulexite or boron pentahydrate as activators, not only compared to the reference sample but also traditional cementitious systems.
Citation - WoS: 28
Citation - Scopus: 31
A New Parameter Influencing the Reaction Kinetics and Properties of Fly Ash Based Geopolymers: A Pre-Rest Period Before Heat Curing
(Elsevier, 2021) Durak, Ugur; Ilkentapar, Serhan; Karahan, Okan; Uzal, Burak; Atis, Cengiz Duran
In this study, the influence of a pre-rest period before heat curing (as a new parameter), on the physical properties, flexural and compressive strength, and microstructure of geopolymer mortars and pastes produced with alkali activation of fly ash were investigated. In this context, geopolymer mortar and paste samples were prepared and pre-rested under laboratory conditions for 0, 1, 2, 3, 7, 14, and 28 days before heat curing. After the pre-rest period, the samples were subjected to heat curing at 75 degrees C in an oven, for 2 days. Mortar and paste samples exposed to a pre-rest period while in the fresh state before heat curing were compared with control samples without pre-resting. Water absorption, porosity, specific gravity, capillarity, flexural strength, compressive strength, and abrasion resistance tests were conducted on the geopolymer mortar samples. A reaction kinetics study using an isothermal calorimeter, XRD, and SEM analyses were performed on the geopolymer paste samples for microstructural investigations. Based on the results obtained, it was observed that the mechanical strength of the samples subjected to the pre-rest period before heat curing increased considerably compared to the reference (without pre-resting) samples. In addition, because of pre-resting, the capillarity coefficient, water permeability, and porosity of the samples decreased compared to the reference samples, and it was concluded that pre-resting improves durability-related properties. Moreover, the reaction kinetics and SEM analysis results, supporting the above findings, showed that a pre-resting period increases the geopolymeric reaction products and causes a denser microstructure.
Citation - WoS: 73
Citation - Scopus: 78
Influence of NaNo SiO2 and NaNo CaCo3 Particles on Strength, Workability, and Microstructural Properties of Fly Ash-Based Geopolymer
(Ernst & Sohn, 2020) Durak, Ugur; Karahan, Okan; Uzal, Burak; Ilkentapar, Serhan; Atis, Cengiz Duran
The influence of nano SiO2(NS) and CaCO3(NC) particles on the properties of class F fly ash based geopolymer mortar activated with different sodium ion concentrations have been investigated. Mortar mixture proportions were 1:3:0.3 for binder, sand, and water, respectively. Nano SiO2 and CaCO3 particles were replaced with a binder by weight basis at the ratios of 1, 2, and 3% in the mixtures. Sodium concentrations amount used were 8, 10, and 12% Na+ of binder content. Geopolymer mortar samples were cured at 60, 75, and 90 degrees C in a furnace for 24, 48, and 72 hr. After the heat curing process, flexural, and compressive strength tests were performed. The changes in the microstructure of geopolymer due to influence of nanoparticles were examined by utilizing isothermal calorimetric studies on geopolymer paste, and field-emission scanning electron microscopy (FESEM). Based on laboratory work results, it was concluded that for all sodium ion concentrations, the addition of nano SiO2 and CaCO3 particles improved the flexural and compressive strengths after 24 hr heat curing. However, the favorable effects of nanoparticles on strength properties tend to disappear after 48 and 72 hr heat curing. The results of isothermal calorimetric studies showed that nano SiO2 and CaCO3 particles accelerated the geopolymeric reactions at an early age. FESEM results showed that additions of nanoparticles made the microstructure of geopolymer products more intense and compact.
Citation - WoS: 1
Citation - Scopus: 1
The Influence of Cement Kiln Dust on Strength and Durability Properties of Cement-Based Systems
(Springer Heidelberg, 2022) Hakkomaz, Hadiye; Yorulmaz, Hediye; Durak, Ugur; Ilkentapar, Serhan; Karahan, Okan; Atis, Cengiz Duran
Citation - WoS: 6
Citation - Scopus: 7
Evaluation of Diatomite Substitute With Thermal Power Plant Waste Fly Ash in Sustainable Geopolymer Through Life Cycle Assessment
(Springer, 2025) Ilkentapar, Serhan; Orklemez, Ezgi; Durak, Ugur; Gulcimen, Sedat; Bayram, Savas; Uzal, Nigmet; Atis, Cengiz Duran
This research demonstrates the potential of diatomite as a fly ash replacement to improve mechanical properties and environmental sustainability and presents it as a viable alternative for sustainable construction. Additionally, a life cycle assessment (LCA) was conducted on the produced mortars to quantitatively compare their environmental impacts using a cradle-to-gate approach. In mixtures, it was used by replacing the diatomite in the ratios of 1%, 2%, 3%, 4%, and 5% by weight of the fly ash. Workability, unit weight, flexural and compressive strength, abrasion resistance, elevated temperature resistance and microstructure analysis were carried out. The results indicated that replacing 1%, 2%, and 3% diatomite increased the compressive and flexural strength of mortars due to their higher specific surface area. Two percent replacement of diatomite provided the best results. FESEM results of 3% diatomite inclusion showed more intense and compact microstructure of geopolymer. Diatomite inclusion increased the abrasion resistance of geopolymer. Since 2% diatomite replacement was found to be optimum, the LCA results showed that geopolymer mortar with 2% diatomite has 25% lower impacts in terms of global warming potential and 10% lower impacts in terms of terrestrial ecotoxicity than conventional Portland cement mortar.
Citation - WoS: 6
Citation - Scopus: 6
The Influence of Cement Kiln Dust on Strength and Durability Properties of Cement-Based Systems
(Springer Heidelberg, 2022) Hakkomaz, Hadiye; Yorulmaz, Hediye; Durak, Ugur; Ilkentapar, Serhan; Karahan, Okan; Atis, Cengiz Duran
There are very few studies in the literature on the usage of CKD in cementitious systems. This article presents the laboratory study results on the influence of cement kiln dust (CKD) on the properties of mortar made with cement kiln dust and Portland cement. The article aims to prevent CKD's (known as a hazardous waste product) damage to nature by utilizing CKD in cementitious systems and contributing to sustainability by reducing cement amount in the cementitious system. For this purpose, 5%, 10%, 15%, and 20% of CKD were replaced with cement and binary cementitious systems were formed. For all mortar mixes, the water/binder ratio was kept constant at 0.5, and the sand/binder ratio was 3. Workability, dry unit weight, water absorption ratio and porosity, flexural strength, compressive strength, abrasion, carbonation, and high-temperature resistance tests were performed on the mortar specimens. Based on the results of laboratory work, it was observed that the replacement of CKD with cement reduces the workability of fresh mortar. Compressive and flexural strengths of CKD-added mixtures were found to be equivalent or insignificantly lower than that of the control sample. The addition of CKD had a negligible effect on water absorption and porosity of samples. Besides, the residual compressive strength determined after the elevated temperature test for the sample made with CKD were found to be equivalent or higher compared to the control sample. Present laboratory studies showed that utilization of CKD in cementitious mortar system is feasible in terms of testing conducted.
Citation - WoS: 6
Citation - Scopus: 6
Reaction Kinetics and Properties of Pumice-Based Geopolymer Systems Cured at Room Temperature
(Elsevier Sci Ltd, 2023) Kucukyildirim, Enver; Yorulmaz, Hediye; Durak, Ugur; Ilkentapar, Serhan; Uzal, Burak; Karahan, Okan; Atis, Cengiz Duran
This research investigated the kinetics of pumice-based geopolymer systems and their physical and mechanical properties. The effect of the Na2SiO3/NaOH ratio of geopolymer systems on the rate of heat evolution and total heat of reaction were examined via isothermal calorimetry of geopolymer pastes prepared with Na2SiO3/NaOH ratios of 2.5, 3, and 3.5. Hardened pastes were also studied with thermo-gravimetric analysis to determine weight loss. In addition, the unit weights and compressive strengths of the pastes prepared using pumice were measured. Although the hydration process starts the earliest in pumice-based geopolymer pastes with a Na2SiO3/ NaOH ratio of 2, they have the lowest total hydration temperature. Na2SiO3/NaOH ratio of 2.5 by mass, shows higher weight loss obtained from TGA results. The compressive strength of the paste sample, prepared with a Na2SiO3/NaOH ratio of 3.5 by mass, was the highest, with 36.30 MPa at 28d. Depending on the Na2SiO3/NaOH ratio, it is thought that as the amount of Na2SiO3 increases in the samples, silica gel formation increases in later ages.