Browsing by Author "Durak, Uğur"

Now showing 1 - 2 of 2

Effects of Dry Particle Coating With Nano-and Microparticles on Early Compressive Strength of Portland Cement Pastes
(Tulpar Academic Publishing, 2021) Yorulmaz, Hediye; Özuzun, Sümeyye; Uzal, Burak; İLkentapar, Serhan; Durak, Uğur; Karahan, Okan; Atis, C. D.
It is known that nano-and microparticles have been very popular in recent years since their advantages. However, due to the very small size of such materials, they have very high tendency to agglomeration particularly for nanoparticles. Therefore, it is critical that they are properly distributed in the system to which they are added. This paper investigated the effects of dry particle coating with nano-and microparticles to solve the agglomeration problem. For a clear evaluation, paste samples were preferred to detemine the compressive strength. Nano-SiO2 and nano-CaCO3, microCaCO3 and micro-SiO2, also known as silica fume, were selected as particulate additives. It was studied by the addition of various percentages (0.3, 0.7, 1, 2, 3 and 5%) of nano-and microparticles in cementitious systems, replacing cement by weight with and without dry particle coating. Dry particle coating was made by using a highspeed paddle mixer. Portland cement and additive particles were mixed at 1500 rpm for 30 seconds in high-speed powder mixer designed for this purpose. The 3-day compressive strength of the cement-based samples to which particles were added at the specified rates was determined and the effect of the dry particle coating on the early strength was investigated. According to the results, it was observed that the production of paste with the dry particle coating technique gave higher compressive strength compared to the production of paste directly in early period. Especially with dry particle coating, compressive strength increased more than 100% in paste samples containing 0.3% nano-SiO2 compared to direct addition without coating. © 2024 Elsevier B.V., All rights reserved.
Citation - Scopus: 1
Comparison of Mechanical and Physical Properties of Screed With and Without Expanded Polystyrene (EPS) Particles
(Yildiz Technical University, 2022) Kiliç, Fikret Merih; Yorulmaz, Hediye; Özuzun, Sümeyye; Durak, Uğur; İLkentapar, Serhan; Karahan, Okan; Atis, C. D.
In this study, in order to observe the mechanical and physical properties of ordinary screed, sandy-lightweight screed and lightweight screed samples, expanded polystyrene (EPS) was used as fine aggregate and lightweight screed systems were produced by replacing sand at 100%, 50% and 0%. Samples of cement dosages of 250, 300, 350 kg/m3 were produced for lightweight screeds, sandy-lightweight screeds and ordinary screeds. Unit weight, water absorption capacity, flexural strength, compressive strength, fire resistance, abrasion and thermal conductivity tests were performed on the produced screed systems. As a result of the research, it was determined that as EPS ratio increases in screed system; unit weights decreased, water absorption rates increased. Besides, the flexural and compressive strengths, fire and abrasion resistance are also decreased. However, it was observed that the thermal conductivity coefficient reduced with the increment of EPS particles in the screed. In normal, sandy-lightweight and lightweight screeds, it was determined that as the cement dosage increased; the unit weights, flexural and compressive strengths, fire and abrasion resistance increased, water absorption capacity and the thermal conductivity coefficient decreased. © 2022 Elsevier B.V., All rights reserved.