Alkali activation of mortars containing different replacement levels of ground granulated blast furnace slag
(ELSEVIER SCI LTD, 2012) Bilim, Cahit; Atis, Cengiz Duran; 0000-0003-3459-329X; AGÜ, Mühendislik Fakültesi, İnşaat Mühendisliği Bölümü; Atis, Cengiz Duran
The aim of the present study is to investigate some properties of alkali-activated mortars containing slag at different replacement levels. Ground granulated blast furnace slag was used at 0%, 20%, 40%, 60%, 80% and 100% replacement by weight of cement, and liquid sodium silicate having three different Na dosages was chosen as the alkaline activator. In this research, carbonation resistance measurements and compressive and flexural strength tests were performed on the mortar specimens with size of 40 40 160 mm. The findings obtained from the tests showed that carbonation depth values of the mortars decreased with the increase of activator dosage. Additionally, compressive and flexural strength values increased with the increase in activator concentration and slag replacement level. Portland cement/slag mortars activated by liquid sodium silicate exhibited lower strength than the slag alone activated by the same activator.
Influence of admixtures on the properties of alkali-activated slag mortars subjected to different curing conditions
(ELSEVIER SCI LTD, 2013) Bilim, Cahit; Karahan, Okan; Atis, Cengiz Duran; Ilkentapar, Serhan; 0000-0003-3459-329X; AGÜ, Mühendislik Fakültesi, İnşaat Mühendisliği Bölümü; Atis, Cengiz Duran
This paper presents the influence of shrinkage-reducing (SHR) and superplasticizing and set-retarding admixtures (SSRe) on the properties of slag pastes and mortars activated by liquid sodium silicate with different dosage and modulus ratio. Properties in the fresh and hardened state for these binders were investigated by means of measuring some properties including setting time, flowability, flexural strength, compressive strength, carbonation and shrinkage. In this study, fifteen pastes and mortars were prepared. Liquid sodium silicate was used to activate the slag at two sodium concentrations, 4% and 6% by mass of slag. Liquid sodium silicate and sodium hydroxide were blended to obtain 0.75 and 1 modulus ratio of SiO2/Na2O. Results showed that although the higher percentage of sodium in the activator produced a higher strength, workability and setting times rapidly decreased with the higher sodium concentration due to instantaneous reaction and quick hardening of slag activated by liquid sodium silicate. None of the admixtures generally had an impact on the setting times of alkali-activated slag (AAS) pastes. SSRe admixture increased the flow rate of AAS mortars while SHR admixture partially affected the flow values of AAS mortars. SHR admixture exhibited a slight decrease in the carbonation depths of AAS mortars. SSRe and particularly SHR chemical admixtures reduced the shrinkage of AAS mortars. However, the shrinkage values of AAS mortars still were higher than those of ordinary Portland cement (NPC) mortars. Curing conditions had a significant effect on the mechanical behavior in the hardened state of AAS mortars compared to NPC mortars